Abstract: "Thirty-four uranium ingots containing controlled amounts of carbon, nitrogen, and Mgl2 slag were cast, rolled, and examined to investigate the relation between these impurities and the quality of the rolled rod. Carbon in concentrations up to 1400 ppm and nitrogen up to 170 ppm, either singly or in combination, had no significant effect on the number of defects observed in the rolled rod. The quality of the rods, however decreased with increasing amount of slag necessary to cause observable differences in the rod could not be detected on analysis, but was visible in the microstructure."

"An investigation of the chemical effects of 1-Mev electrons on BrF3 at 25 degrees C has been carried out. Pressure measurements taken during the irradiation suggest the presence of Br2 and BrF5 as decomposition products and a fractional distillation of the irradiated liquid confirmed their presence. The extent of decomposition was determined both by fraction distillation and spectrophotometric methods. The radiation effect seemed to reach saturation when approximately 10 per cent of the BrF3 was destroyed. The exposure necessary for the decomposition products to reach a concentration of half the saturated value was calculated to be 2.7 microampere hours/cc BrF3 while the "G" value was found to be 1.5. A qualitative comparison of irradiation dosages from the Statiltron with that expected from spent fuels revealed that little decomposition of BrF3 reagent is to be expected from 1-say cooled Hanford fuel (in pile for 100 days) while in the case of 1-day cooled MTR type fuel (in pile for 12 days) a saturated effect might be realized in 1-3 hours. Since at most only 10 per cent of the BrF3 is destroyed it is concluded that BrF3, from a radiation resistance standpoint, is a suitable standpoint, is a suitable reagent for …

Abstract: The sandstones and conglomerates contained in the Shinarump conglomerate stratigraphic level in the area along Colorado River between the Moab and Dewey bridges have been assigned to the lower Chinle. One small anomaly was located, but no favorable radioactive areas were found. Gray-green mudstone and siltstone zones and carbonated material are absent.

Abstract: Uranium was discovered in the Gas Hills of the Wind River Basin by Mr. Nail E. McNeice of Riverton, Wyoming while he was prospecting with a Geiger counter in September 1953. Field parties of the Atomic Energy Commission started work in the area in October 1953.

From abstract: "The state of reduction of wet process phosphoric acid determines largely the extractability of its uranium content. This report defines the economic relationships involved over a wide range of reduction of the acid. Reductant consumption, penalties and capital investment as well as solvent consumption are evaluated."

Abstract: "Observations of refracted sound waves from atomic tests at the Nevada and Pacific Proving Grounds are evaluated to show temperature and winds in the ozonosphere. A simplified method of making these interpretations is presented to reduce the computation work load normally associated with atmospheric sound studies."

This report follows an investigation with the purpose of studying the operational characteristics of a catalytic tube recombiner where the gases are passed over stainless steel tubes coated with platinum black.

From introduction: "As a part of this program, this report presents the results of a study of an interacting system in which the conditions for criticality are given in terms of the concentration of fissionable material and the geometry of the system."

At present there are three Laboratories actively engaged in analyzing samples for the "SUNSHINE PROGRAM"; Lamont Geological Observatory, University of Chicago and the New York Health and Safety Laboratory. The U.S. Department of Agriculture Laboratories at Beltsville ae preparing samples for the University of Chicago, and are running normal strontium analyses. In order that the results reported from each of the three laboratories may be used to evaluate Sr90 distribution, a cooperative program has been in operation since August of 1953. This preliminary report lists the results on samples received and distributed by HASL. It is hoped that complete results from all laboratories will be available soon.

From abstract: "Performance data were obtained for the TNX replacement evaporator when operated within the limits imposed by a new control system. This system was designed to avoid conditions which might lead to a repetition of an earlier explosion due to inclusion of organic material in the uranyl nitrate-nitric acid system, which was heated to elevated temperature. The true heat transfer coefficient was found to be 280 BUT/hr-ft2-ºF for all concentrations of solutions to be evaporated in the plant, and will allow operation at design capacities."

"The composition of the solder for the solder plug has been set as the tin-silver eutectic. Final tests on this solder show that life expectancies much longer than 6 months are probable with the current design. The design of the heater tube to contain the solder plug has been settled. This consists of a copper tube impregnated with U235O2. Arrangements have been made to have test specimens fabricated by powder metallurgy techniques. The equipment for the MTR in-pile test of trigger element response times has been largely completed and tested. The design of the complete inner capsule for the BF3 safety element has been developed as well as the cladding technique. Mock-up elements have been tested in the Hanford test reactor to determine the control that may be obtained with elements of this type, although the analysis of the results has not been made. Prototype elements are also ready for testing in the test pile, except for loading with B10F3. Experiments have been designed and submitted for approval for production pile tests of prototype."

"In this review and critique of many matters, most of them related to a central scheme, namely the outlining of methods and procedures in the Commission, ore-finding technique, new empirical criteria as guides to analyses of grade, ore realization factors, and many other subjects that have a bearing on our field methods used have been treated."

A series of two-dimensional airfoils were run through a complete 360 ° angle of attack range to determine their low-speed force characteristics. The airfoils were chosen in an attempt to vary as many parameters (such as thickness, camber, thickness distribution, etc.) as possible with the limited number of shapes that time permitted. All airfoils tested had lift curves with two distinct stalls and quite similar drag curves between 0 ° and 90 ° angle of attack. The highly cambered sections developed peculiar characteristics in the inverted and trailing edge forward positions, as might be expected. The effective test Reynolds number of 0.81 x 10(6) based on the model chord of one foot.

The description of the thick-target neutron yields from the D(t,n)He4 and the D(d,n)He3 reactions is calculated as a function of the energy of the bombarding particles. For 60-kev particles the ratio is 108. I increases to 168 at 100 Kev and to 194 for 120-kev particles. A qualitative discussion of the yields from various deuterium target leads to the conclusion that the greatest yield would come from the target which has the lowest stopping cross section per deuterium atom.