This semi-annual technical progress report describes work performed at Morehouse College under DOE Grant No. DE-FG26-02NT15447 during the period April 01, 2004 to September 30, 2004 which covers the fourth six months of the project. Presently work is in progress to characterize phase and emulsion behavior for ethylbenzene/water/ethanol system. Ethylbenzene that has the equivalent carbon number is used as the model condensate. During this reporting period, work was under way and the electrical conductivity experimental system was set up at the Atlanta University Center. Following the set-up of the emulsion measurement system, the electronic instruments and data acquisition modules involved were tested for proper operation of the system. Then, the conductivity output was normalized with that obtained for 10mM NaCl water. Radial coreflooding experiments with ethanol injection prior to and after water injection were completed to assess the effectiveness of the surfactant flooding in the recovery of condensate by our industrial partner, Surtek, CO, in this reporting period. In Run 1, 10 mM NaCl without ethanol injection recovered 31.5% of the initial ethyl benzene saturation. Injection of ethanol following 10 mM NaCl produced a tertiary ethyl benzene bank with maximum ethyl benzene cuts of 32%. In Run 2, 50 vol% …

This semi-annual technical progress report describes work performed at Morehouse College under DOE Grant No. DE-FG26-02NT15447 during the period October 01, 2004 to March 31, 2005 which covers the fifth six months of the project. Presently work is in progress to characterize phase and emulsion behavior for ethylbenzene/water/ethanol system. Ethylbenzene that has the equivalent carbon number is used as the model condensate. During this reporting period, electrical conductivity measurements for bottom, and top phases, as well as bottom/top, and top/bottom conjugate pair phases of the ethylbenzene/water/ethanol system were performed for various ethanol volume percentage of the mixtures starting from 2% to 60%. Preliminary findings are that electrical conductivity of the bottom phase decreased as ethanol volume fraction of the mixture increased. Conductivity of the top phase was small and remained almost the same for variations in ethanol volume fraction of the mixture. Conductivity of the emulsion of the conjugate pair phases decreased as the fraction of volume of the top phase was increased and vice versa. Also inversion phenomena was observed. Detailed analyses are in progress including the prediction of conductivity data using the theoretical model already developed in this project.