Summary. A test rig has been designed to obtain basic two phase forced convection liquid metal heat transfer and pressure drop data for use in the design of liquid metal boilers. This engineering report includes background of the boiling problem, partial summary of work done by other investigators, the object, scope, engineering, and operations of this test rig, and a summary of reproducibility tests conducted in a water back-up rig.

This technical report is a summary of short time strength data for CS1830 series Cb-1Zr material. The data are presented as a function of fabrication history or the amount of cold work received during fabrication. Three fabrication categories were considered for comparison: forgings and extrusions; bar, plate, rod and pipe; and sheet and tubing. Forgings and extrusions having received no cold work showed the highest strength over the entire temperature range 68F to 2800F; bar, plate, rod and pipe received moderate cold work and showed lower strength than forgings and extrusions but higher strength than sheet and tubing in the temperature range 2000F to 2800F.

The linear thermal expansion of thirteen tungsten carbide cermets with cobalt binder was investigated experimentally over the temperature range from 68 to 1800 F. Cobalt contents varied from 2.5 to 60 per cent. Several compositions included additions of mixed carbides of titanium, tantalum, and columbium. The experimentally observed coefficients of thermal expansion for the various compositions were compared with coefficients analytically computed from the coefficients for the constituents. Three such analytical methods were evaluated. In one method, the coefficient of expansion of the mixture was computed by volume fractions and in a second method by weight fractions. In the third method, the computation accounted for the stresses set up in the mixture by the difference in thermal expansion of the carbide skeleton and the cobalt binder. The expansions of all these cermets agreed with the values computed by weight fractions or by the stress method within 12 per cent, and by volume fractions within 28 per cent. The cermets containing less than one per cent mixed carbides agreed with the expansion computed either by weight fractions or by stress within 8 per cent, the cermets containing more than five per cent mixed carbides agreed with values computed by volume fractions …