Abstract: "The ductility of Type 310 stainless steel T-joints brazed with GE-62 brazing alloy was measured at room temperatures 1200, 1650, and 1800 F. The measure of ductility was taken as the plastic axial strain required to crack braze fillets in T-section tensile specimens. At elevated temperatures, the ductility of as-brazed joints approximated that of the stainless steel, but at room temperature the brazed joints had only one-tenth the ductility of the base metal. Annealing for 16 hr at 1800 F in air was found to triple the room-temperature ductility of the brazed joint."