From introduction: "This report describes the second phase of the work on the application of protective coatings to uranium by vapor deposition to reduce or prevent its corrosion by water."

Abstract: "Refinement of grain size of the base uranium-chromium eutectic alloy (uranium-5 w/o chromium) by ternary additions is discussed. Thirteen additions to the base alloy were investigated, and three additions were found to exhibit worthwhile grain-refinement tendencies. The three alloys, uranium-5 w/o chromium-0.2 w.o molybdenum, uranium-5 w/o chromium-0.2 w/o germanium, and uranium-5 w/o chromium-0.2 w/o niobium, were heat treated to produce final grain-size structures of between 0.015 and 0.033 mm."

The following report focuses on an investigation made to determine if vacuum melting was an absolutely necessary step in the metallurgical process of melting and casting uranium.

Abstract: "A study of plastic flow during the extrusion of tubing was made by extruding colored Plasticine billets in a small-scale extrusion press. Decreasing the included angle of the conical die and tapering the ram end of the billet decreased the amount of coextrusion of the backer block into the tubing, lubricating the billet also decreased coextrusion."

The following report studies the dissolution of aluminum-canned thorium, providing results that suggest a dissolution cycle that permits the separation of the canned-slug components.