"A series of high urania-content glasses were fiberized and examined for high-temperature strength properties. One glass, RX360 containing 60% U/sub 3/O/ sub 8/ by weight, had better high-temperature tensile properties than any glass previously reported. It was observed that many of the glasses studied separated into immiscible phases and that the fiberizable glass phase had lower U/sub 3/O/ sub 8/ content than the base compositions. A physical analysis of crystal structures of the devitrification products from the nuclear fuel glasses indicated that most of the crystals consisted of uranium oxide in a reduced state. By adding O/sub 2/ to molten glass, it was possible to eliminate most of this devitrification. By elimination of crystals, the fiberizing of the glass was more uniform and the glasses produced had more consistent physical properties."

"Properly designed and fitted respirators have been effective devices for reducing the inhalation of toxic aerosols. The degree of protection afforded by these devices has not been quantitatively measured under actual work conditions except by bioassay or other elaborate techniques. This report describes a new quantitative technique for evaluating over-all respiratory performance under conditions comparable to exposure to highly toxic radioactive materials such as plutonium and non-radioactive materials such as beryllium."

Abstract: This technical report contains a description and results of a second series of critical experiments performed on the SM-2 core mock-up, as additional to the first series of experiments reported in APAE No. 54. The SM-2 core mock-up contains 36.4 kg U-235 and and estimated 67.9 gm B-10. The equivalent diameter and the active height are about 22 in.; the metal-to-water volume ration is 0.344. Data is presented on activation, reactivity, and stuck rod measurements. All measurements were conducted on the open seven control rod array employing 38 stationary fuel elements. Activation measurements consisted of neutron flux measurements using uranium fission foils for relative power distribution studies, the effect of flux suppressors on reducing power peaks, blocked coolant channel measurements, and gamma ray dose distribution. Reactivity measurements were performed to determine the effect f flow divider, flux suppressors and stimulated high temperature and pressure operation; b-10 loading in the SM-2 core; and core material coefficients. For the later, the worth in cents per gm or cents per cc was determined at simulated temperature of 510 degree F for B-10, U-235, stainless steel, and void. Stuck rod measurements were made to obtain an indication of the criticality margin in the …

In the Sulfex process, stainless steel cladding, generally 304-L, is removed from fuel elements by dissolution in boiling four to six molar sulfuric acid. When cladding removal is complete, the decladding solution is removed is removed to waste. The exposed fuel cores are rinsed and dissolved in nitric acid.

This report describes progress made in the study of the feasibility of the concept, plant arrangement studies, and considerations pertaining to partial plant attendance. It is concluded that both the indirect and direct boiling cycles are feasible. The recommended reference design is the direct cycle, in a single capsule, with the turbine, generator and pumps on a single shaft.