From introduction: This is Progress report BMI-282, the first of a series covering the operation of the pressure-leaching towers for the extraction of uranium by an ammonium carbonate leach...This report discusses the data obtained from tests run to show the effects of such variables as the amount of air and carbon dioxide passed through the pulp, temperature, pressure, and concentration of ammonium carbonate and ammonium bicarbonate in the leach solution on the extraction of uranium.

This report covers the progress made on an intensive program to develop and evaluate UO2 as a possible fuel element for the PWR.

Abstract: "Sound, fabricable ingots of thorium were produced by triple are melting of electrolytic thorium. Consumable electrodes were fabricated by tack welding of cold-pressed and vacuum-sintered bars of the granular thorium electrodeposited from a molten-salt bath. The hydrogen content of the electrodeposited material was reduced from 80 to 4 ppm by vacuum sintering at 1250 C at pressures below 1 x 10-(-3) mm of mercury. Both sodium and chlorine content were reduced during melting; sodium from 250 to 25 ppm and chlorine from 1000 to 30 ppm. Oxygen and HCl acid-insoluble contents increased during sintering and melting. Oxygen content increased from 0.35 to 0.50 w/o and HCl acid-insoluble content from 0.8 to 4.0 w/o. A starlike includion revealed by metallographic examination of the as-cast thorium was identified as ThO2."