The following report is the third Quarterly Report in a series whose investigative purpose is to determine the extent to which zirconium and zirconium alloys exhibit delayed failure as caused by a combination of absorbed hydrogen and applied stress.

The following quarterly report covers the period during February 16 to May 15, 1963. This report is divided into sections covering the separate activities during this period, studying the thermal behavior of the F-center in RbCl.

Abstract: The boron-carbon equilibrium diagram has been determined by X-ray, metallographic, and thermal analysis of sintered and arc-cast alloys. A single carbide having a range of solubility from approximately 9 to 20 a/o carbon and melting congruently exists in the system. The terminal solubility of carbon in boron is 0.1-0.2a/o. The freezing reaction at the composition and melting temperature of elemental boron; there is a eutectic reaction at 29a/o carbon and 2375 degrees Celcius. No allotropy of boron was observed.

This is the fourth quarterly report that documents a system of mass flow that can record measurements of homogeneous flow, slurries, highly corrosive fluids and multiphase fluids, additionally considering pressure drops, measuring external to the flow, ruggedness and reliability.

Quarterly report describing progress on a project to develop and evaluate high-temperature tungsten alloys. This report discusses properties for specific base alloys at room temperature and under high temperatures.