From introduction: "This report is concerned with exploratory experiments designed to studies the efficiency of a number of scavengers for zirconium and niobium adsorption and to provide preliminary information on the best conditions to employ on the most satisfactory of those scavengers studied, namely Super Filtrol FO. The data in this report include data obtained through October, 1949, and are by no means considered to be final. The investigation is currently being actively continued."

Abstract:"The creep resistance of various uranium binary alloys was investigated at 1500 and 1800 F in vacuum. Tests were made on alloys of uranium with beryllium, columbium, molybdenum, tantalum, titanium, and zirconium and on molybdenum-UO2 composites. Of the alloys examined, those of the uranium-molybdenum system exhibited the best creep resistance. At 1500 F, creep rates of about 0.005%/hr were produced in uranium-molybdenum alloys by a stress of 2500 psi and, at 1800 F, similar creep rates were obtained in composites of 90 wt % molybdenum-10 wt % UO2 by a stress of 12,000 psi."

Abstract: "Aluminum-clad nickel-plated uranium is corrosion resistant in boiling water. Samples with intentional defects in the aluminum-nickel clodding layers, after testing for more than 300 hr. showed no sign of rapid failure. The study of electroplated metals on uranium for aluminum cladding has defined the effects of several processing variables on the corrosion resistance. The quality of the uranium and the quality of the aluminum-nickel bond were important. Heat treatment and vacuum outgassing of the nickel-plated uranium prior to aluminum cladding were beneficial, and minimizing the amount of air present in the hot-press assembly was desirable. Variation in the steps for electroplating on uranium did not affect the corrosion resistance of aluminum-clad uranium."

Introduction: "The uranium-5 w/o chromium alloy has been intensively investigated for use in a power reactor in the as-cast condition. However, when cast sample fuel elements were subjected to irradiation, their stability was found to be unsatisfactory. In order to improve the behavior of the alloy, a program of grain refinement by heat treatment was begun. The effect of chill casting on the heat-treated grain size was also investigated."

The following report follows an investigation made to determine the composition of uranium-rich ternary eutectic alloys most suitable for reactor application in the as-cast condition. These determinations were made based metallographic examination and thermal analysis of as-cast alloys.

Abstract: "An experimental study was made to determine the effective shielding provided by a modern reinforced-concrete office building (AEC Headquarters building) from nuclear fallout. Pocket ionization chambers were used for measurement of the radiation-field strength. Fallout was simulated with distributed and point-source configurations of Co-60 and Ir-192 sources. Four typical sections were selected for study, and experiments were performed on each. These included an external wing with exposed basement walls and an external wing with a buried basement. Roof studies were made on an internal wing with a full basement and on the east end of wing A, which has a thin-roof construction. The thick-roof construction of 8 in. of concrete and 2 in. of rigid insulation covers all the building except the east end of wing A, which has 4 in. of concrete and 2 in. of insulation."

Abstract: "A method for determining hydrogen in lithium hydride by heating samples with lead at 600 C, was developed. The hydrogen evolved during thermal decomposition of the hydride is purified and oxidized to water with cupric oxide at 400 C. The analysis is completed by collecting and weighing this water. Success in development of the analytical procedure has depended upon a careful design and assembly of equipment for handling samples in a dry, inert atmosphere. For seven pure hydride samples analyzed by the recommended method the estimates of the standard deviation varied between 0.12 and 0.41 percent lithium hydride (or 1.3 and 4.2 parts per thousand) for 8 to 18 determinations on each sample. The procedure is relatively insensitive to variations in certain conditions. For single-piece samples weighing 0.2 to 0.5 gram it was found to be more satisfactory than a method which uses mercury in place of lead for sample decomposition. For powdered lithium hydride samples the lead and mercury methods are equally satisfactory."

Monthly report the progress and development of improved zirconium alloys for service in superheated water and steam. This report covers the period between April 1 to April 31, 1961 and was conducted by the United States and the European Atomic Energy Community (EURATOM).

From summary: "Methods were developed for measuring various engineering properties of high-density concretes. Data are presented on selected thermal properties of a limonite-iron concrete and the mechanical properties of the limonite-iron concrete, a magnesium oxychloride concrete, and a Portland cement concrete containing steel punchings and shot (no limonite)."

Abstract: "A quantitative method for the determination of individual rare earths in thorium down to a level of 0.05 ppm, is described. The procedure consists of a chromatographic cellulose-columns separation followed by a solution-type spectrographic determination. Values are given for the recovery of a number of rare earths using this combined procedure."

Abstract: "This report describes the results of X-ray diffraction examination of reaction products from a series of experiments performed by Mallinckrodt Chemical Works as an acid in understanding the process of bomb reduction of UF4. UF4 is initially reduced to UF3 by magnesium at 560 C., and subsequently to metal at 600 C. MgF2 from the initial reaction forms a coating on the magnesium which retards the final spontaneous reaction."

The following report examines the fission counter, fission plates and activation results of the neutron energy distribution in the center of the Los Alamos plutonium reactor.

The operation of the Fast Reactor is considered in terms of normal equilibrium conditions and normal shut-down. The proposed loading, control rod adjustment and subsequent "floating" operation are discussed. Safety devices and interlocks are described. Temperature and reactivity changes are examined with respect to various system failures, phase changes, and "flashing" of the reactor. Slow changes due to faulty slug cooling are also considered. The calculations were initially based upon 10 kw operation. Performance tests of the mercury system now indicate that 20-kw operation may be feasible.

Abstract: "Decontamination factors of the order of 10-4 were obtained for Beta and Gamma emitters present as fission products when uranium was precipitated from 50 mC activity level solutions as uranyl oxalate under normal uranium yield conditions for three cycles (~60%). Factors of the order of 10-3 were obtained by the use of this reaction with similar solutions under relatively high uranium yield conditions for three cycles (~90%). The uranium peroxide precipitation reaction proved to be of no value on such solutions, yielding decontamination factors of only 17.1 Beta emitters and 1.2 for Gamma emitters for three cycles."

The following report describes procedures taken to utilize the photelometer to procure the most rapid and reliable determinations, but the goal of the tests presented was to create satisfactory dispersions of particles to analyze.

"The magnetic properties of color centers were studied to obtain information regarding electron traps in insulators. Experiments designed to determine the equation governing the recovery of resonance after saturation were carried out. Relatively large samples were prepared by the method of additive coloration. KCl and RbCl crystals were used. Resonance saturation as a function of concentration was investigated and no significant dependence found. Measurements of the unsaturated susceptibility were made at liquid nitrogen and liquid helium temperatures. The bleaching of the F-center to form the B-band produced a different resonance. The equipment for observing the saturation and recovery of a portion of the resonance at 4 deg K is described. A theoretical examination was made of the interaction between the vibration of the ions around a negative-ion vacancy in an alkali halide and an electron trapped at that site. (M.C.G.)."

Abstract: "The niobium-carbon system has been determined by X-ray and metallographic examination of sintered and arc-cast alloys. Two carbides exist: hexagonal Nb2C with a limited range of homogeneity, and cubic NbC with a solubility range from 8.25 to 10.25 weight per cent carbon. Dilute alloys freeze by eutectic reaction at 2230 C. The solubility of carbon in niobium is 0.80 at the eutectic temperature, but this decreases rapidly with temperature. Metallographic evidence indicates a peritectic reaction between melt, Nb2C, and NbC; alloys richer in carbon than NbC freeze by eutectic reaction."

The following report is the final technical report on a series of reports under contract AT(11-1)-515, titled "Niobium Phase Diagrams", covering the period from April 15, 1957 to April 16, 1960.

The following report follows the studies of electroplating on uranium and concurrent metallurgical clodding.

This report follows investigations of methods for sealing the ends of stainless steel-uranium oxide fuel pins with the objective to develop an end-capping method that would give consistently good-quality closures in production.

This report analyzes Parian and Teflon that were exposed to solutions of 1AX, 1AS, and 1AF, ANL June 1, 1948 Flowsheet, under conditions described in the following report.

The following report provides results from laboratory tests on the corrosion resistance of various types of stellite facings on astenitic stainless steel T-347 to Redox streams.

Abstract: "The elastic double scattering of deuterons by complex nuclei has been investigated experimentally. Measurements were made on carbon, aluminum, and copper at around 157 Mev; on lithium, beryllium, and carbon at around 125 Mev; and on carbon and aluminum at 94 Mev. The expected tensor components of the deuteron polarization have not been observed. Measurements have been made of the differential cross section and vector-type polarization as a function of angle for the scattering of deuterons from the above elements, at the above energies. The observed polarizations were larger than would be expected on the basis of the individual nucleon-nucleus interactions. In a second experiment we measured the 169-Mev proton-proton polarization at 10, 15, 22.5, 30, and 35 in the laboratory system. The results indicate that partial waves up to and including L = 3 are important at this energy."

The following report describes a gaseous scintillation counting system, including the production and operation of the counter.