From introduction: "This investigation was undertaken with the general objective of determining whether uranium core could be sheathed with aluminum by an extrusion-cladding process. The ultimate objective of this work was to determine the feasibility of extrusion cladding flat plates of uranium."

Abstract: "Aluminum-clad nickel-plated uranium is corrosion resistant in boiling water. Samples with intentional defects in the aluminum-nickel clodding layers, after testing for more than 300 hr. showed no sign of rapid failure. The study of electroplated metals on uranium for aluminum cladding has defined the effects of several processing variables on the corrosion resistance. The quality of the uranium and the quality of the aluminum-nickel bond were important. Heat treatment and vacuum outgassing of the nickel-plated uranium prior to aluminum cladding were beneficial, and minimizing the amount of air present in the hot-press assembly was desirable. Variation in the steps for electroplating on uranium did not affect the corrosion resistance of aluminum-clad uranium."

This report covers the progress made on an intensive program to develop and evaluate UO2 as a possible fuel element for the PWR.

From abstract: Results of a study of the sanitary engineering aspects of fallout from nuclear weapons are reported. Data were obtained from: a. Weekly surface water samples from 22 stations on streams and reservoirs in Eastern Massachusetts, collected from March, 1952 to July, 1953, and assayed for radioactivity. b. Weekly rain samples from March to July, 1953. c. Stream mud and soil samples collected before and after a large fallout. d. Results of fallout activity measurements by others based on samples from Massachusetts and the vicinity of Rochester, New York. Plots are presented showing the relations of the radiological data to the timing of detonations and the daily precipitation and showing daily deposition of activity and concentration in runoff. Runoff coefficients for fallout radioactivity are calculated.

Abstract: "Sound, fabricable ingots of thorium were produced by triple are melting of electrolytic thorium. Consumable electrodes were fabricated by tack welding of cold-pressed and vacuum-sintered bars of the granular thorium electrodeposited from a molten-salt bath. The hydrogen content of the electrodeposited material was reduced from 80 to 4 ppm by vacuum sintering at 1250 C at pressures below 1 x 10-(-3) mm of mercury. Both sodium and chlorine content were reduced during melting; sodium from 250 to 25 ppm and chlorine from 1000 to 30 ppm. Oxygen and HCl acid-insoluble contents increased during sintering and melting. Oxygen content increased from 0.35 to 0.50 w/o and HCl acid-insoluble content from 0.8 to 4.0 w/o. A starlike includion revealed by metallographic examination of the as-cast thorium was identified as ThO2."

Abstract: "Refinement of grain size of the base uranium-chromium eutectic alloy (uranium-5 w/o chromium) by ternary additions is discussed. Thirteen additions to the base alloy were investigated, and three additions were found to exhibit worthwhile grain-refinement tendencies. The three alloys, uranium-5 w/o chromium-0.2 w.o molybdenum, uranium-5 w/o chromium-0.2 w/o germanium, and uranium-5 w/o chromium-0.2 w/o niobium, were heat treated to produce final grain-size structures of between 0.015 and 0.033 mm."

The following report focuses on an investigation made to determine if vacuum melting was an absolutely necessary step in the metallurgical process of melting and casting uranium.

Abstract: "The analysis of an immobilized plasma is here extended to the case where the geometry is cylindrical rather than Cartesian. (This report, UCRL-4439 (Rev, 4 constitutes Part II of the report series (UCRL-4466, Parts I, III, and IV) dealing with this general problem.)"

Abstract: "The reflections of microwaves from the walls of a plasma-containing vessel are studied. The probable cause of the reflections is discussed, and several suggestions are made for eliminating the reflections from the waveguide in the vessel and particularly from the pyrex vessel wall and copper tubing surrounding the pyrex. Quarter-wave-thick carbon-filled plastics or glasses having a very low vapor pressure room most promising when placed inside the pyrex cylinder. BaTiO3 appears to be an excellent material when placed outside the vacuum."

The following report proposes various methods in injecting and heating in mirror machines, using high-energy ion beams.

Abstract: "The possibility of transient temperature variations during the self-heating of a plasma by thermonuclear reactions was investigated. Calculations were performed on an IBM Card Program Calculator. Estimates of the time scale for self-heating were obtained. It was concluded that it would be unsafe to assume that the nuclear temperature is always equal to or greater than the electron temperature in a discussion of plasma instabilities for a plasma with 10 percent or greater tritium concentration."

This report describes a method used to determine semi-quantitatively the time-varying plasma density in magnetic mirror machines by microwave phase-shift and attenuation measurement.

Abstract: "Two parallel wires close together with an arc between them form a hairpin-type of current configuration which should magnetically propel the plasma of the arc. By the time-of-flight measurements with probes it has been demonstrated that directed translational energies of 290 ev can be imparted to deuterons in a plasma produced by a high-current pulsed arc at the tips of two titanium wires loaded with deuterium. It is believed that three deuterons are actually magnetically propelled."

Abstract: "A scheme is discussed in which D+ ions would be accelerated to about 100 kev in a conventional accelerator, then be sent through a gas target frmo which about half the ions would emerge neutral with very little scattering or energy loss; the neutral beam would then cross into a magnetic field and part of the atoms would be ionized and trapped by colliding with the already trapped ions. The smallest mirror machine with a central field of 30-40 kilogauss, 2;1 mirror ratio and β = 01 to 0.5 that would trap most of the neutral beam in the steady state, would be about a meter in diameter and require the order of hundreds of amperes of D+ ions into the neutralizer. The smallest stellerator with a field of 30 kilogauss and β = 0.1 that would trap most of the neutral beam would be about a meter long and require about 10 amperes of D+ ions. A preliminary mirror machine experiment that might be done using the 1/2-ampere, 100-kev D+ beam from the UCRL spare MTA injector is discussed. A method of starting these machine is discussed."

From introduction comments: The present analysis is intended to examine the relations for "adiabatic" injection in general from a different point of view.

Abstract: "The deuterium plasma which is ejected by a 6000-ampere pulsed current through a rail-type spark source has a yield in the forward direction which is a factor of 5 to 10 greater than that in the perpendicular direction. This effect is believed to be due to the magnetic propulsion of the plasma."

Abstract: Several uranium occurrences have been discovered in the Coso lake beds, Owens Valley, California, along the west flank of the Coso Range.

Introduction: Rabon Creek in Laurens County, South Carolina and Big Generostee Creek in Anderson County, have large established flood plains. Preliminary investigations by the U.S. Geological Survey showed the presence of monazite in these streams, and the areas were recommended for detailed investigation.

Abstract: Ten days were spent during June 1955, examining the sedimentary rocks along the San Juan and Colorado Rivers between Mexican Hat, Utah, and Lee's Ferry, Arizona. The most favorable area for uranium deposits occurs in the Shinarump member of the Chinle formation between Clay Hills Crossing and Spencer Camp along the San Juan River. Mineralization is spotty and deposits are small and almost all below ore-grade. Only one small mine, the Whirlwind, is currently producing ore. Gray-green alteration of the underlying Moenkopi is moderately developed in the vicinity of the Whirlwind mine; elsewhere alteration is weakly developed.

From introduction: This report is written in response to a request from the Army Engineers for an appraisal of the uranium potential of the area included in the Yams Test Station. the area of Proposed Expansion of the Yuma Test Station, and the Williams Bombing and Gunnery Range. Only the area covered by the present Yuma Test Station is included here. The other areas will be discussed In subsequent reports.

Abstract: A low-level airborne radiometric survey of the younger pre-Cambrian Dripping Spring quartzite, undertaken in the mountainous region lying roughly 100 riles east of Phoenix, was completed June 3, 1955. Twenty-seven radioactive anomalies were located. To date seven of these have produced uranium ore, four more will probably become producers, and six others may possibly become producers. Flying was concentrated in the Dripping Spring quartzite, but reconnaissance flights were made over other formations. Private prospecting, both from the air and on the ground, increased considerably when the airborne project started. Eleven of the private discoveries have produced ore, and many others show considerable promise.

From foreword: The objective of this study is to determine the practical and economic use of nuclear for the production of electric power in the Pittsburgh district.

Abstract: A part of the Green River Basin airborne reconnaissance project, re: memo to Phillip L. Merritt, March 12, 1954, Proposed Airborne Reconnaissance Project, Green River Basin, Wyoming, was completed during the months from July though October 1954. No uranium mineralization of commercial value was found.

Abstract: Secondary uranium minerals occur along narrow silicified northeast-trending fractures in Tertiary volcanics of rhyolitic composition. Two zones containing uranium minerals are present.