The current study focuses on phase stability and evolution in the titanium-zinc titanium-copper and titanium-antimony systems. The study utilized the Laser Engineering Net Shaping (LENS™) processing technique to deposit compositionally graded samples of three binary system in order to allow the assessment of phase stability and evolution as a function of composition and temperature the material is subjected to. Through LENS™ processing it was possible to create graded samples from Ti-xSb (up to 13wt%) and Ti-xCu (up to 16wt%). The LENS™ deposited gradient were solutionized, and step quenched to specific aging temperature, and the resulting microstructures and phase were characterized utilizing XRD, EDS, SEM, FIB and TEM. The Ti-Zn system proved incapable of being LENS™ deposited due to the low vaporization temperature of Zn; however, a novel processing approach was developed to drip liquid Zn onto Ti powder at temperatures above β transus temperature of Ti (882 ◦C) and below the vaporization temperature of Zn (907 ◦C). The product of this processing technique was characterized in a similar way as the graded LENS™ depositions. From measurements performed on Ti-Sb it seems that Sb could be a potential α stabilizer in Ti due to the presence of a mostly homogeneous α …

Polymer nanocomposites are a going part of Materials Science and Engineering. These new composite materials exhibit dimensional and thermal stability of inorganic materials and toughness and dielectric properties of polymers. Development of nanocomposites become an important approach to create high-performance composite materials. In this study silica, fly ash, silica nanotubes and carbon black particles have been added to modify polyurethane foam and thermoplastic polyurethanes. It has been found that the addition of silica can diminish the size of foam bubbles, resulting in an increased stiffness of the material, increase of the compressive strength, and greater resistance to deformation. However, the uniformity of bubbles is reduced, resulting in increased friction of the material. Fly ash added to the foam can make bubbles smaller and improve uniformity of cells. Therefore, the material stiffness and compressive strength, resistance to deformation, and has little impact on the dynamic friction of the material. Adding nanotubes make bubble size unequal, and the arrangement of the bubble uneven, resulting in decreased strength of the material, while the friction increases. After the addition of carbon black to the polyurethane foam, due to the special surface structure of the carbon black, the foam generates more bubbles during the foaming …

Since their discovery in the 1930s, polymeric foams have been widely used in the industry for a variety of applications such as acoustical and thermal insulation, filters, absorbents etc. The reason for this ascending trend can be attributed to factors such as cost, ease of processing and a high strength to weight ratio compared to non-foamed polymers. The purpose of this project was to develop an “indestructible” material made of polycarbonate (PC) for industrial applications. Due to the high price of polycarbonate, two foaming methods were investigated to reduce the amount of material used. Samples were foamed physically in supercritical CO2 or chemically with 5-phenyl-1H-tetrazole. After thermal characterization of the foams in differential scanning calorimetry (DSC), we saw that none of the foaming methods had an influence on the glass transition of polycarbonate. Micrographs taken in scanning electron microscopy (SEM) showed that foams obtained in physical and chemical foaming had different structures. Indeed, samples foamed in supercritical CO2 exhibited a microcellular opened-cell structure with a high cell density and a homogeneous cell distribution. On the other hand, samples foamed with 5-phenyl-1H-tetrazole had a macrocellular closed-cell structure with a much smaller cell density and a random cell distribution. Compression testing showed …

Mg alloys have spurred a renewed academic and industrial interest because of their ultra-light-weight and high specific strength properties. Hexagonal close packed Mg has low deformability and a high plastic anisotropy between basal and non-basal slip systems at room temperature. Alloying with Li and other elements is believed to counter this deficiency by activating non-basal slip by reducing their nucleation stress. In this work I study how Li addition affects deformation mechanisms in Mg using atomistic simulations. In the first part, I create a reliable and transferable concentration dependent embedded atom method (CD-EAM) potential for my molecular dynamics study of deformation. This potential describes the Mg-Li phase diagram, which accurately describes the phase stability as a function of Li concentration and temperature. Also, it reproduces the heat of mixing, lattice parameters, and bulk moduli of the alloy as a function of Li concentration. Most importantly, our CD-EAM potential reproduces the variation of stacking fault energy for basal, prismatic, and pyramidal slip systems that influences the deformation mechanisms as a function of Li concentration. This success of CD-EAM Mg-Li potential in reproducing different properties, as compared to literature data, shows its reliability and transferability. Next, I use this newly created potential …

The relatively low oxidation resistance and subsequent surface embrittlement have often limited the use of titanium alloys in elevated temperature structural applications. Although extensive effort is spent to investigate the high temperature oxidation performance of titanium alloys, the studies are often constrained to complex technical titanium alloys and neither the mechanisms associated with evolution of the oxide scale nor the effect of oxygen ingress on the microstructure of the base metal are well-understood. In addition lack of systematic oxidation studies across a wider domain of the alloy composition has complicated the determination of composition-mechanism-property relationships. Clearly, it would be ideal to assess the influence of composition and exposure time on the oxidation resistance, independent of experimental variabilities regarding time, temperature and atmosphere as the potential source of error. Such studies might also provide a series of metrics (e.g., hardness, scale, etc) that could be interpreted together and related to the alloy composition. In this thesis a novel combinatorial approach was adopted whereby a series of compositionally graded specimens, (Ti-xMo, Ti-xCr, Ti-xAl and Ti-xW) were prepared using Laser Engineered Net Shaping (LENS™) technology and exposed to still-air at 650 °C. A suite of the state-of-the-art characterization techniques were employed to assess …

In-situ x-ray photoemission (XPS) and ex-situ FTIR studies of nanoporous organosilicate glass (OSG) films point to the separate roles of radicals vs. VUV photons in the carbon abstraction. The studies indicate that reaction with O2 in presence of VUV photons (~123 nm) result in significant carbon abstraction within the bulk and that the kinetics of this process is diffusion-limited. In contrast, OSG exposed to atomic O (no VUV) results in Si-C bond scission and Si-O bond formation, but this process is self-limiting after formation of ~1 nm thick SiO2 surface layer that inhibits further diffusion. Therefore, the diffusion-dominated kinetics of carbon abstraction observed for OSG exposed to O2 plasma is definitively attributed to the diffusion of O2 down OSG nanopores, reacting at photo-activated sites, rather than to the diffusion of atomic O. Pretreatment of OSG by 900 eV Ar+ ion bombardment also results in formation of 1 nm thick SiO2-like surface overlayer that inhibits O2 diffusion, inhibiting VUV+O2 and O2 plasma-induced reactions, and that the effectiveness of this treatment increases with ion kinetic energy. On the contrary, organosilicate glass (OSG) films with backbone carbon (-Si-R-Si-) exhibit significantly enhanced resistance to carbon loss upon exposure to O2 plasma, radicals and VUV+O2 …

The effect of friction stir processing (FSP) on the mechanical wear behavior was investigated for Ti-1Al-8V-5Fe (Ti-185) and stainless steel (Incoloy® A-286) alloys. The Ti-185 and A-286 alloys were tested in different processing conditions, including as rolled (AR), AR+FSP, and AR+FSP+aged. A high frequency reciprocating rig was used to simulate fretting-type wear of these alloys at room temperature. The Vickers micro-hardness and wear rates were calculated and compared for each processing condition. It was determined that along with increasing hardness in the stir zones, FSP resulted in improved wear resistance for both alloys. Specifically, wear rates in the stir zones were reduced to lowest values of 1.6 x 10-5 and 5.8 x 10-7 mm3/N·m for the AR+FSP+aged Ti-185 and A-286 alloys, respectively, despite lower hardness for A-286 alloy. Mechanistic studies were conducted to determine the reason behind these improvements in wear resistance and the effect of FSP on the microstructural evolution during wear. For the Ti-185 alloy, x-ray diffraction revealed that there was a phase transformation from β-Ti (AR+FSP) to α-Ti (AR+FSP+aged). This phase decomposition resulted in the harder and stiffer Ti phase responsible for lowering of wear rate in Ti-185. While x-ray diffraction confirmed the A-286 alloy retains its …