Baeyer-Villiger oxidation of 1-methylpentacyclo[5.4.0.02,6.03,10.05,9] undecane-8,11-dione, performed by using m-chloroperbenzoic acid in 1:1 molar ratio, resulted in the formation of monolactone. The corresponding dilactone, was synthesized by reacting 1-methyl-PCU-8,11-dione with m-chloroperbenzoic acid in 1:2 molar ratio. 6-Methyl-1,4,4a,8a-tetrahydro-1,4-methanonaphthalene-5,8-dione was converted into the corresponding exo-6,7-monoepoxide via treatment with 30% aqueous hydrogen peroxide. Epoxidation of this monoepoxide by using m-chloroperbenzoic acid afforded the corresponding bis-epoxide. Ceric ammonium nitrate (CAN) promoted oxidation of 1-methyl-PCU-8,11-dione afforded "methylated lactones" and a "methylated alkene."

Baeyer-Villiger oxidation of 1,9-dibromopentacyclo[5.4.0.02,6.03,10.05,9]undecane-8,11-dione (1,9-dibromo-PCU-8,11-dione) was performed by using an excess amount of m-chloroperbenzoic acid (3 equivalents) and resulted in the formation of the corresponding monolactone. The reaction would not proceed to the dilactone stage. The structure of the reaction product was established unequivocally via single crystal X-ray diffraction. Baeyer-Villiger oxidation of 1,9-dibromo-PCU-8,11-dione using ceric ammonium nitrate (CAN) was also performed and afforded a mixture of lactones. Only one of these lactones, which also contained an alkene functionality, could be isolated and characterized. 1,7-dibromo-PCU-8,11-dione was also reacted with CAN, yielding the mono-lactone, which has also been characterized.

Nanocrystalline praseodymium oxide films have been successfully generated on stainless steel substrates. The electrochemical deposition was performed in the cathode compartment of a divided electrochemical cell with a regular three-electrode configuration. The green films obtained by electrodeposition were then annealed at high temperatures for 1-3 hours. X-ray diffraction revealed the fluorite structure of Pr6O11 and the crystallite size was calculated. X-ray photoelectron spectroscopy was employed to study the composition of the oxide films and also the oxidation state of Pr. Scanning electron microscopy was utilized to study the surface texture and microstructure of deposits. Fourier transform infrared spectrometery was used to investigate the composition of the films. The effects of different conditions on the green films were also studied such as different pH values of the electrolyte solution, different deposition modes, different supporting electrolytes and different applied current densities. Sintering experiments were conducted to investigate the properties of the green films. Praseodymium oxide powders were also successfully prepared by combining electrochemical methods with sintering processes. The praseodymium oxide powders were characterized by X-ray diffraction and Fourier transform infrared spectroscopy. The crystallite sizes of the powders were evaluated.