This problem in lieu of thesis report describes a practical photolithographic method to produce micro patterns on metal-oxide-semiconductor or metal-oxide-semiconductor-metal layers for electrical measurements. The desired patterns are then transferred from the photo mask to the photoresist-coated metal film by exposure, followed by wet etching. In the procedure described in this report, it was observed that microstructures as small as 27 mm with an edge roughness of ~ 2 mm can be reproducibly generated with this process. MOS capacitors and transistors structures can be fabricated by using this technique. The method described in this report requires access to only simple facilities so that it is relatively inexpensive, and the overall time required for the whole process is short.

Throughout history consumer products were generally manufactured from wood and metal. They either had to hold their natural color or become subject to painting. When plastics entered the industry, it was recognized for its ease of shaping, re-usability, physical properties and its low cost. One of plastics' greatest benefits is its ability to hold a given color from within allowing it to avoid use of paint. This paper will give a brief overview on the effects of pigments when incorporated in a polyolefin. It will provide a classification of the main types of pigments and how each effect the properties of the product through: crystallization, weatherability, opacity, coloristic values and of course viscosity.