Ceramics have a wide variety of applications due to their unique properties; however, the low fracture toughness leads the formation and propagation of unpredictable cracks, and reduces their reliability. To solve this problem, self-healing adaptive oxides were developed. The aim of the work is to gain new insights into self-healing mechanisms of ceramics and their application. Binary oxide systems were investigated that are at least partially healed through the extrinsic or intrinsic addition of silver or silver oxide to form ternary oxides (e.g., Nb2O5 + Ag → AgNbO3). Sintered pellets and coatings were tested. For self-healing TBCs, model systems that were studied include YSZ-Al2O3-SiC, YSZ-Al2O3-TiC, YSZ-Al2O3-Nb2O5, and YSZ-Al2O3-Ta2O5. Laser cladded samples and sintered pellets were produced to test. The healing process occurs due to the formation of oxidation products and glassy phases depending on the self-healing mechanism. X-ray diffraction was used to explore phase evolution, chemical compositions, and structural properties of these samples. SEM equipped with EDS was used to investigate the chemical and morphological properties for the cross-sectional area. Pin-on-disc test was applied to test tribology performance for Nb2O5-Ag2O system, and infiltration test was applied to test CMAS-resistance for TBCs at elevated temperature. The improvements in the performance of …

The current work investigates how the interactions among constituent elements in high entropy alloys or complex concentrated alloys (HEA/CCAs) can lead to lattice instability and local chemical ordering which in turn affects the microstructure and properties of these alloys. Using binary enthalpies of mixing, the degree of ordering in concentrated multi-component solid solutions was successfully tailored by introducing Cr, Al and Ti in a CoFeNi HEA/CCA. CoFeNi was selected as the base alloy to achieve a close to random solid solution as indicated by the near-zero binary enthalpies in CoFeNi alloy system. The room temperature tensile properties of these alloys with varied degree of ordering follow a consistent trend where yield stress increased with degree of ordering. This novel approach provides a new alloy design strategy to obtain controlled ordering tendencies and consequently targeted mechanical properties. Further studies on specific alloys have been conducted to utilize this ordering tendency in attaining precipitation strengthening. For this purpose, Al, Ti and Ni were selected to promote ordering and Co, Fe, and Cr were chosen to strengthen the solid solution matrix. In Al0.25CoFeNi HEA/CCA, the ordering tendency between Al and Ni results in a competition between two long-range ordered phases, L12 and B2. …