During the reporting period, work continued on development of formulations using the materials down-selected from the initially identified contenders for the fibrous monolith wear resistant components. In the previous reporting period, a two-stage binder removal process was developed that resulted in prototype parts free of voids and other internal defects. During the current reporting period, work was performed to characterize the two-stage binder removal process for WC-Co based FM material systems. Use of this process has resulted in the fabrication of defect free sintered WC-Co FM bodies, with minimal free carbon porosity and densities approaching 100% theoretical. With the elimination of free carbon porosity and other binder removal process related defects, development work focused on optimizing the densification and eliminating defects observed in WC-Co based FM consolidated by pressureless sintering. Shrinkage of the monolithic core and shell materials used in the WC-Co based FM system was measured, and differences in material shrinkage were identified as a potential cause of cell boundary cracking observed in sintered parts. Re-formulation of material blends for this system was begun, with the goal of eliminating mechanical stresses during sintering by matching the volumetric shrinkage of the core and shell materials. Thirty-three 7/8 inch drill bit …