Technical report. From Abstract : "Reaction of NbBr5 and niobium metal in a sealed tube under a temperature gradient from 410° to 350° gave NbBr4 in good yields. However, an increase in the higher temperature from 410° to 450° was sufficient to eliminate NbBr4 as a product and cause deposition of a lower bromide."

Technical report. From Abstract : "The necessary conditions for preparation of TaBr4 and TaI4 by reduction of the pentahalides with tantalum or aluminum metal in a sealed tube under a controlled temperature gradient have been demonstrated."

From abstract: "Resistivities of solid solution alloys in the systems Gd-Lu, Tb-Lu, Gd-Er, and Y-Lu were measured from 4.2-320°K to determine the behavior of the resistivity in alloy systems with magnetic phenomena arising from localized magnetic moments. A large contribution to the residual resistivity is caused by the random distribution of these localized moments through the lattice. An analysis of the lattice resistivity of the metals shows large variations across the heavy rare-earth series which are possibly correlated with the change of c/a ratio of the metals and the attendent changes in the Fermi surface geometry."