In studies of the fabrication of fuel subassemblies for the supercritical-water reactor, the limited ductility of stainless steel-UO₂ fuel sheet made the fabrication of corrugated-flat-plate-type subassemblies impractical. A fabricable MTR-type assembly, 5/8 in. square and 30 in. long, was developed. Methods for edge cladding fuel sheet were developed and a brazing alloy, GE-75, was found to be corrosion resistant in supercritical water.

Abstract: "Thirty-four uranium ingots containing controlled amounts of carbon, nitrogen, and Mgl2 slag were cast, rolled, and examined to investigate the relation between these impurities and the quality of the rolled rod. Carbon in concentrations up to 1400 ppm and nitrogen up to 170 ppm, either singly or in combination, had no significant effect on the number of defects observed in the rolled rod. The quality of the rods, however decreased with increasing amount of slag necessary to cause observable differences in the rod could not be detected on analysis, but was visible in the microstructure."

A report intended to aid in the evaluation of solid-state bonding techniques for cladding natural-uranium fuel-element cores with aluminum, tensile specimens which are 1/4 in. in diameter and 3 in. long.