Corrosion represents the single most frequent cause for product replacement or loss of product functionality with a 5% coat to the industrial revenue generation of any country in this dissertation the efficacy of using filled coatings as a protection coating are investigated. Fillers disrupt the polymer-substrate coating interfacial area and lead to poor adhesion. Conflicting benefits of increasing surface hardness and corrosion with long term durability through loss of adhesion to the substrate are investigated. The effects of filler type, filler concentration and exposure to harsh environments such as supercritical carbon dioxide on salt water corrosion are systematically investigated. The constants maintained in the design of experiments were the substrate, AISI-SAE 1018 steel substrate, and the corrosive fluid synthetic sea salt solution (4.2 wt%) and the polymer, Bismaleimide (BMI). Adhesion strength through pull-off, lap shear and shear peel tests were determined. Corrosion using Tafel plots and electrochemical impedance spectroscopy was conducted. Vickers hardness was used to determine mechanical strength of the coatings. SEM and optical microscopy were used to examine dispersion and coating integrity. A comparison of fillers such as alumina, silica, hexagonal boron nitride, and organophilic montmorillonite clay (OMMT) at different concentrations revealed OMMT to be most effective with …

Electrically conductive fabrics are one of the major components of smart textile that attracts a lot of attention by the energy, medical, sports and military industry. The principal contributors to the conductivity of the smart textiles are the intrinsic properties of the fiber, functionalization by the addition of conductive particles and the architecture of fibers. In this study, intrinsic properties of non-woven carbon fabric derived from a novel linear lignin, poly-(caffeyl alcohol) (PCFA) discovered in the seeds of the vanilla orchid (Vanilla planifolia) was investigated. In contrast to all known lignins which comprise of polyaromatic networks, the PCFA lignin is a linear polymer. The non-woven fabric was prepared using electrospinning technique, which follows by stabilization and carbonization steps. Results from Raman spectroscopy indicate higher graphitic structure for PCFA carbon as compared to the Kraft lignin, as seen from G/D ratios of 1.92 vs 1.15 which was supported by a high percentage of graphitic (C-C) bond observed from X-ray photoelectron spectroscopy (XPS). Moreover, from the XRD and TEM a larger crystal size (Lc=12.2 nm) for the PCFA fiber was obtained which correlates to the higher modulus and conductivity of the fiber. These plant-sourced carbon fabrics have a valuable impact on zero …