Electrically conductive fabrics are one of the major components of smart textile that attracts a lot of attention by the energy, medical, sports and military industry. The principal contributors to the conductivity of the smart textiles are the intrinsic properties of the fiber, functionalization by the addition of conductive particles and the architecture of fibers. In this study, intrinsic properties of non-woven carbon fabric derived from a novel linear lignin, poly-(caffeyl alcohol) (PCFA) discovered in the seeds of the vanilla orchid (Vanilla planifolia) was investigated. In contrast to all known lignins which comprise of polyaromatic networks, the PCFA lignin is a linear polymer. The non-woven fabric was prepared using electrospinning technique, which follows by stabilization and carbonization steps. Results from Raman spectroscopy indicate higher graphitic structure for PCFA carbon as compared to the Kraft lignin, as seen from G/D ratios of 1.92 vs 1.15 which was supported by a high percentage of graphitic (C-C) bond observed from X-ray photoelectron spectroscopy (XPS). Moreover, from the XRD and TEM a larger crystal size (Lc=12.2 nm) for the PCFA fiber was obtained which correlates to the higher modulus and conductivity of the fiber. These plant-sourced carbon fabrics have a valuable impact on zero …

Natural fibers like kenaf, hemp, flax and sisal fiber are becoming alternatives to conventional petroleum fibers for many applications. One such applications is the use of Non-woven bio-fiber mats in the automobile and construction industries. Non-woven hemp fiber mats were used to manufacture plywood in order to optimize the plywood structure. Hemp fiber mats possess strong mechanical properties that comparable to synthetic fibers which include tensile strength and tensile modulus. This study focuses on the use of hemp fiber mat as a core layer in plywood sandwich composite. The optimization of fiber mat plywood was done by performing a three factor experiment. The three factors selected for this experiment were number of hemp mat layers in the core, mat treatment of the hemp mat, and the glue content in the core. From the analysis of all treatments it was determined that single hemp mat had the highest effect on improving the properties of the plywood structure.

Fiber-metal laminates (FML) are the advanced materials that are developed to improve the high performance of lightweight structures that are rapidly becoming a superior substitute for metal structures. The reasons behind their emerging usage are the mechanical properties without a compromise in weight other than the traditional metals. The bond remains a concern. This thesis reviews the effect of pre-treatments, say heat, P2 etch and laser treatments on the substrate which modifies the surface composition/roughness to impact the bond strength. The constituents that make up the FMLs in our present study are the Aluminum 2024 alloy as the substrate and the carbon fiber prepregs are the fibers. These composite samples are manufactured in a compression molding process after each pre-treatment and are then subjected to different tests to investigate its properties in tension, compression, flexural and lap shear strength. The results indicate that heat treatment adversely affects properties of the metal and the joint while laser treatments provide the best bond and joint strength.