The nuclear waste package design for Yucca Mountain (Nevada, USA), in its current configuration, consists of a double wall cylindrical container fabricated using a highly corrosion resistant Ni-based Alloy 22 for the outer barrier and type 316 stainless steel for the inner structural vessel. A mailbox-shaped drip shield fabricated primarily using Ti Grade 7 will cover the waste packages. The environmental degradation of the relevant materials have been extensively studied and modeled for over ten years. This paper reviews the state-of-the-art understanding of the degradation modes of Alloy 22 (N06022) due to its interaction with the predicted in-drift mountain conditions including temperature and types of electrolytes. Subjects discussed include thermal aging and phase stability, dry oxidation, general and localized corrosion, stress corrosion cracking and hydrogen induced cracking.

Alloy 22 is a nickel base alloy highly resistant to all forms of corrosion. In conditions where tight crevices exist in hot chloride containing solutions and at anodic potentials, Alloy 22 may suffer crevice corrosion, a form of localized attack. The occurrence (or not) of crevice corrosion in a given environment (e.g. salt concentration and temperature), is governed by the values of the critical potential (E{sub crit}) for crevice corrosion and the corrosion potential (E{sub corr}) that the alloy may establish in the studied environment. If E{sub corr} is equal or higher than E{sub crit}, crevice corrosion may be expected. In addition, it is generally accepted that as Alloy 22 becomes passive in a certain environment, its E{sub corr} increases and its corrosion rate (CR) decreases. This paper discusses the evolution of E{sub corr} and corrosion rate (CR) of creviced Alloy 22 specimens in six different mixtures of sodium chloride (NaCl) and potassium nitrate (KNO{sub 3}) at 100 C. The effect of immersion time on the value of E{sub crit} was also determined. Two types of specimens were used, polished as-welded (ASW) and as-welded plus solution heat-treated (ASW+SHT). The latter contained the black annealing oxide film on the surface. Results …