Baeyer-Villiger oxidation of 1-methylpentacyclo[5.4.0.02,6.03,10.05,9] undecane-8,11-dione, performed by using m-chloroperbenzoic acid in 1:1 molar ratio, resulted in the formation of monolactone. The corresponding dilactone, was synthesized by reacting 1-methyl-PCU-8,11-dione with m-chloroperbenzoic acid in 1:2 molar ratio. 6-Methyl-1,4,4a,8a-tetrahydro-1,4-methanonaphthalene-5,8-dione was converted into the corresponding exo-6,7-monoepoxide via treatment with 30% aqueous hydrogen peroxide. Epoxidation of this monoepoxide by using m-chloroperbenzoic acid afforded the corresponding bis-epoxide. Ceric ammonium nitrate (CAN) promoted oxidation of 1-methyl-PCU-8,11-dione afforded "methylated lactones" and a "methylated alkene."

Semiconductor circuitry feature miniaturization continues in response to Moore 's Law pushing the limits of aluminum and forcing the transition to Cu due to its lower resistivity and electromigration. Copper diffuses into silicon dioxide under thermal and electrical stresses, requiring the use of barriers to inhibit diffusion, adding to the insulator thickness and delay time, or replacement of SiO2 with new insulator materials that can inhibit diffusion while enabling Cu wetting. This study proposes modified amorphous silicon carbon hydrogen (a-Si:C:H) films as possible diffusion barriers and replacements for SiO2 between metal levels, interlevel dielectric (ILD), or between metal lines (IMD), based upon the diffusion inhibition of previous a-Si:C:H species expected lower dielectric constants, acceptable thermal conductivity. Vinyltrimethylsilane (VTMS) precursor was condensed on a titanium substrate at 90 K and bombarded with electron beams to induce crosslinking and form polymerized a-Si:C:H films. Modifications of the films with hydroxyl and nitrogen was accomplished by dosing the condensed VTMS with water or ammonia before electron bombardment producing a-Si:C:H/OH and a-Si:C:H/N and a-Si:C:H/OH/N polymerized films in expectation of developing films that would inhibit copper diffusion and promote Cu adherence, wetting, on the film surface. X-ray Photoelectron Spectroscopy was used to characterize Cu metallization of …

The square-planar tetracyanonickelate(II) anion was intercalated into 2:1 and 3:1 Mg-Al layered double hydroxide systems (LDHs). In the 2:1 material, the anion holds itself at an angle of about 30° to the layers, whereas in the 3:1 material it lies more or less parallel to the layers. This is confirmed by orientation effects in the infrared spectra of the intercalated materials and by X-ray diffraction (XRD) data. The measured basal spacings for the intercalated LDH hosts are approximately 11 Å for the 2:1 and approximately 8 Å for the 3:1. The IR of the 2:1 material shows a slight splitting in the ν(CN) peak, which is suppressed in that compound's oriented IR spectrum, indicating that at least some of the intercalated anion's polarization is along the z-axis. This effect is not seen in the 3:1 material. A comparison between chloride LDHs and nitrate LDHs was made with respect to intercalation of tetracyanonickelate(II) anions. Both XRD data and atomic absorption spectroscopy (AAS) data of the LDH tetracyanonickelates confirms that there are no significant differences between the products from the two types of starting materials. The presence of a weak ν(NO) peak in the IR spectra of those samples made from nitrate …

Various gold complexes were computationally investigated, to probe their photophysical, geometric, and bonding properties. The geometry of AuI complexes (ground state singlet) is very sensitive to the electronic nature of the ligands: σ-donors gave a two-coordinate, linear shape; however, σ-acceptors yielded a three-coordinate, trigonal planar geometry. Doublet AuIIL3 complexes distort to T-shape, and are thus ground state models of the corresponding triplet AuIL3. The disproportionation of AuIIL3 to AuIL3 and AuIIIL3 is endothermic for all ligands investigated, however, σ-donors are better experimental targets for AuII complexes. For dimeric AuI complexes, only one gold center in the optimized triplet exciton displays a Jahn-Teller distortion, and the Au---Au distance is reduced versus the ground state distance (i.e., two reasons for large Stokes' shifts).

Electrodeposition is a novel method for fabrication of diamond-like carbon (DLC) films on metal substrates. In this work, DLC was electrochemically deposited on different substrates based on an anodic oxidation cyclization of acetylene in liquid ammonia. Successfully anodic deposition was carried out for DLC onto nickel substrate at temperatures below -40°C. Comparative studies were performed on a series of different carbon sources (acetylene, sodium acetylide, and a mixture of acetylene and sodium acetylide). The films were characterized using a variety of methods including Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), XPS valence band spectra, and/or scanning electron microscopy (SEM). Raman spectroscopy is used as a bench mark technique to verify the presence of deposited DLC films, to access the films homogeneities, and to provide the ratio of the different carbon phases, mainly disordered graphite (D) and graphite (G) phases in the films. A combination of the Raman with FTIR and valence band spectra analysis allowed the distinction between hydrogenated DLC and unhydrogenated DLC films. Three different kinds of DLC [(1) hydrogenated DLC (a-C:H); (2) tetrahedral hydrogenated DLC (ta-C:H); and (3) graphitic-like DLC] were deposited depending upon the deposition conditions and substrates. Temperature and current density are …

The reactivity of oxide surfaces and metal-oxide interfaces play an important role in many technological applications such as corrosion, heterogeneous catalysis, and microelectronics. The focus of this research was (1) understanding the effects of water vapor exposure of ultrathin aluminum oxide films under non-ultrahigh vacuum conditions (>10-9 Torr) and (2) characterization of Pt growth modes on ultrathin Ta silicate and silicon dioxide films and the effects of growth modes on adhesion of a Cu overlayer. These studies were conducted with X-ray photoelectron spectroscopy (XPS). Ni3Al(110) was oxidized (10-6 Torr O2, 800K) followed by annealing (1100K). The data indicate that the annealed oxide film is composed of NiO, Al2O3 and an intermediate phase denoted here as "AlOx". Upon exposure of the oxide film at ambient temperature to increasing water vapor pressure (10-6 - 5 Torr), a shift in both the O(1s) and Al(2p)oxide peak maxima to lower binding energies is observed. In contrast, exposure of Al2O3/Al(polycrystalline) to water vapor under the same conditions results in a high binding energy shoulder in the O(1s) spectra which indicates hydroxylation. Spectral decomposition provides further insight into the difference in reactivity between the two oxide films. The corresponding trends of the O(1s)/Ni0(2p3/2) and Al(2p)/Ni0(2p3/2) spectral …

Electrodeposition method is used to deposit diamond-like carbon (DLC) films on copper substrates via anodic oxidation at low temperature. These films are characterized using Raman spectroscopy, Fourier transform infrared spectroscopy and scanning electron microscopy. Homogeneity of these films is studied using Raman spectroscopy and scanning electron microscopy. Scotch tape peel tests indicate adherent film on copper substrate. Carbon phase transformation is studied using thermal annealing experiments in conjunction with Raman spectroscopy and scanning electron microscopy. A cathodic electrochemical method is also studied to deposit diamond-like carbon films on copper substrates. However, films deposited by the cathodic route have poor adhesion and quality compared to anodically deposited films. It is also possible to grow diamond phase on copper substrates using acetylene in liquid ammonia via electrodeposition route. An electrochemical method is proposed for boron doping into DLC films.

The purpose of this thesis is to analyze the thermochemical properties of solutes in nonelectrolyte pure solvents and to develop mathematical expressions with the ability to describe and predict solution behavior using mobile order theory. Solubilities of pesticides (monuron, diuron, and hexachlorobenzene), polycyclic aromatic hydrocarbons (biphenyl, acenaphthene, and phenanthrene), and the organometallic ferrocene were studied in a wide array of solvents. Mobile order theory predictive equations were derived and percent average absolute deviations between experimental and calculated mole fraction solubilities for each solute were as follows: monuron in 21 non-alcoholic solvents (48.4%), diuron in 28 non-alcoholic solvents (60.1%), hexachlorobenzene (210%), biphenyl (13.0%), acenaphthene (37.8%), phenanthrene (41.3%), and ferrocene (107.8%). Solute descriptors using the Abraham solvation model were also calculated for monuron and diuron. Coefficients in the general solvation equation were known for all the solvents and solute descriptors calculated using multilinear regression techniques.

The TaSiO6 films, ~8Å thick, were formed by sputter deposition of Ta onto ultrathin SiO2 substrates at 300 K, followed by annealing to 600 K in 2 torr O2. X-ray photoelectron spectroscopy (XPS) measurements of the films yielded a Si(2p) binding energy at 102.1 eV and Ta(4f7/2) binding energy at 26.2 eV, indicative of Ta silicate formation. O(1s) spectra indicate that the film is substantially hydroxylated. Annealing the film to > 900 K in UHV resulted in silicate decomposition to SiO2 and Ta2O5. The Ta silicate film is stable in air at 300K. XPS data show that sputter-deposited Cu (300 K) displays conformal growth on Ta silicate surface (TaSiO6) but 3-D growth on the annealed and decomposed silicate surface. Initial Cu/silicate interaction involves Cu charge donation to Ta surface sites, with Cu(I) formation and Ta reduction. The results are similar to those previously reported for air-exposed TaSiN, and indicate that Si-modified Ta barriers should maintain Cu wettability under oxidizing conditions for Cu interconnect applications. XPS has been used to study the reaction of tert-butylimino tris(diethylamino) tantalum (TBTDET) with atomic hydrogen on SiO2 and organosilicate glass (OSG) substrates. The results on both substrates indicate that at 300K, TBTDET partially dissociates, forming …

Monodispersed nanoparticles of poly-N-isopropylacrylamide-co-allylamine (PNIPAM-co-allylamine) and PNIPAM-co-acrylic acid (AA) have been synthesized and used as building blocks for creating three-dimensional networks. The close-packed PNIPAM-co-allylamine and PNIPAM-co-AA nanoparticles were stabilized by covalently bonding neighboring particles at room temperature and at neutral pH; factors which make these networks amicable for drug loading and release. Controlled release studies have been performed on the networks using dextran markers of various molecular weights as model macromolecular drugs. Drug release was quantified under various physical conditions including a range of temperature and molecular weight. These nanoparticle networks have several advantages over the conventional bulk gels for controlling the release of biomolecules with large molecular weights. Monodispersed nanoparticles of poly-N-isopropylacrylamide-co-allylamine (PNIPAM-co-allylamine) can self-assemble into crystals with a lattice spacing on the order of the wavelength of visible light. By initiating the crystallization process near the colloidal crystal melting temperature, while subsequently bonding the PNIPAM-co-allylamine particles below the glass transition temperature, a nanostructured hydrogel has been created. The crystalline hydrogels exhibit iridescent patterns that are tunable by the change of temperature, pH value or even protein concentration. This kind of soft and wet hydrogel with periodic structures may lead to new sensors, devices, and displays operating in aqueous …