The rheology of 1-8% hydroxypropyl cellulose (HPC) solutions has been studied in the temperature range of 20-45 degrees Celsius. The results showed that the relative viscosity at each HPC concentration decreases with increasing temperature. The relative viscosity decreases drastically at about 43 degrees Celsius due to a phase transition. The influence of anionic surfactant, sodium dodecylsulfate (SDS), induced gelation of a 2% HPC solution. The HPC solutions gelled at surfactant SDS concentrations ranging from 0.4 to 1.0 critical micelle concentration (CMC). The gelation of the HPC/SDS hydrogel is explained in the surfactant SDD - bridged HPC linear polymer chains. The complex viscosity - concentration profile was determined below the CMC of the SDS - water pair. The peak itself was a function of frequency indicating the presence of two relaxation times within the gelled network.

This problem in lieu of thesis report describes a practical photolithographic method to produce micro patterns on metal-oxide-semiconductor or metal-oxide-semiconductor-metal layers for electrical measurements. The desired patterns are then transferred from the photo mask to the photoresist-coated metal film by exposure, followed by wet etching. In the procedure described in this report, it was observed that microstructures as small as 27 mm with an edge roughness of ~ 2 mm can be reproducibly generated with this process. MOS capacitors and transistors structures can be fabricated by using this technique. The method described in this report requires access to only simple facilities so that it is relatively inexpensive, and the overall time required for the whole process is short.