The picosecond optical response of five thin germanium samples was measured following intense optical excitation using two variations of the excitation and probe technique. Seven-picosecond laser pulses of wavelength 1.054 um were used to measure the optical transmission of the samples for a variety of probe delays, excitation fluences, and sample temperatures. These parametric experiments were performed in an effort to determine if carrier cooling, carrier diffusion, or carrier recombination dominates the carrier dynamics immediately following excitation. The studies of a 5.7 um thick sample indicated that Auger recombination does not dominate the carrier dynamics, but that the carriers most likely cool immediately to within a few optical phonons of the lattice temperature. Lattice heating may also occur depending on excitation level. Neither cooling nor diffusion was ruled out as a major contributor to the transient optical response. A numerical analysis indicated that, although diffusion may be minimized in the thinner samples, the importance of surface recombination increases as the sample thickness decreases. The lattice temperature dependence of the optical transmission was found not to be in disagreement with the known temperature dependence of the low-density diffusion coefficient. Finally, new structure was observed in the data which is consistent with …

This dissertation presents experimental and theoretical studies of transient degenerate four wave mixing (DFWM) in organic dyes. Chapter 1 is an introduction to DFWM. Chapter 2 describes DFWM experiments that were performed in the gain medium of a dye laser. Chapter 3 presents the theory of DFWM of short pulses in three level saturable media. Chapter 4 presents DFWM experiments of femtosecond pulses in the saturable absorber of a passively modelocked ring dye laser. Chapter 5 presents the theory of DFWM of ultrashort pulses in resonant media.

Bulk laser-induced breakdown and self-focusing in single samples of fused quartz and NaCl were examined using picosecond optical pulses at 1.0 ym and 0.5 ym. The results of three separate but related experiments are reported. First the nonlinear index of refraction, n2, of each of the test materials is measured near the respective damage thresholds of the samples. The values of 1*2 were determined by detecting beam distortions in the far field, transmitted laser beam profile caused by the irradiance dependent index of refraction. The experimental traces were compared to theoretical beam profiles generated by a nonlinear propagation code and n2 was extracted from the resulting fits.