Abstract This technical report covers the thermal analysis performed on the SM-1 Core III for both steady state and transient conditions is reported. SM-1 Core III will be used as a test for Type 3 elements in a PM-2A Core. The steady state analysis indicated minimum departure from nucleate boiling ratios (DNBR) for both design and scram conditions above the minimum criteria of 1.5. Local nucleate boiling was noted in the hot internal channels and lattice passage at scram power conditions. Loss of flow transient results indicate DNBR's above 1.5, insuring that the core is safe from burnout. Bulk boiling was noted in the hot channels and lattice passage at scram power condition.

"The influence of compressive creep on the self-diffusivity of α-iron has been measured in the temperature range of 742-885°C. the diffusivity is enchanced in proportion to the strain rate, but this dependence decreases with increasing temperature. The magnitude of the strain is relatively unimportant in this connection. Strain rates from 0 to -2 x 10¯³ sec¯¹ were investigated with a corresponding increase in diffusivity up to 3 x 10³ times. The results are analyzed in terms of vacancy diffusion and the excess vacancies introduced during deformation. It is concluded that grain boundaries are the main vacancy sinks in polycrystalline iron and that the vacancy lifetime is therefore dependent on the grain size."