Abstract: This technical report presents design criteria to prevent the brittle fracture of ferritic reactor vessels that cold occur as a result of the rise in NDT caused by fast neutron irradiation. The criteria require that maximum principal stress in the vessel does not exceed 18 percent of yield stress at temperatures below NDT + 60 degree F. Under certain conditions the allowable stress may be based on the irradiated yield stress. A discussion of brittle fracture and an explanation of the criteria are included.