Experiments showed that 30% tributyl phosphate will not extract acid- deficient species of uranyl nitrate. Flooding throughputs for the Mark I stacked- clone contactor ranged from 600 cc/min organic at zero aqueous to 60 cc/min organic at 1950 cc aqueous. A large electronic vibrator of 5000-lb thrust was found somewhat inferior to pneumatic vibration for compacting oxide fuels into stainless-steel tubes. Tests were started on the use of fixed-bed CuO oxidizers for removing hydrogen contamination from helium gas streams. None of the variables studied within this period effected an increase in particle size in the denitration of thorium nitrate to produce ThO/sub 2/. The rate of uranyl sulfate loading on nitrate equilibrated Dowex 21K appears to be essentially independent of the loading solution sulfate concentration. The nitric acid concentrations corresponding to maximum UO/sub 2/-ThO/sub 2/ pellet dissolution rate were 15.5 M for Thorex solution and 13 M for the adjusted Darex solution. Two additional Semicontinuous Sulfex declad and Thorex core dissolutions of prototype Consolidated Edison fuel assemblies were made to complete the series of runs. The effective area of cylindrical UO/sub 2/ pellets dissolving in nitric acid was estimated from experimental rate measurements as a function of the fraction dissolved. …

A critical review of the literature revealed no experiments on uranyl ion transfer from an aqueous to a tributyl phosphate phase which positively measured the kinetics of the chemical reaction at the interphase. Drawing isorhythmic lines on a three component diagram gives a complex correlation for the compaction of three sizes of glass beads. Neither the use of thoria sols nor high feed solution concentrations of thorium nitrate gave any significant increase in mean particle diameters over those obtained from nitrate solutions of lower concentrations in flame denitration. A hydraulic film resistance has been detected in the anion exchange of uranyl sulfate into Dowex 2lK, and chloride elution was found to give a higher apparent uranium diffusion coefficient than nitrate elution. The rate of dissolution of mixed thorium-uranium oxides was determined as a function of the per cent of mixed oxides dissolved. Mixing in tanks packed with boron glass Raschig rings is being continued. The SRE hydraulic dejacketer has been operated successfully with prototype fuel rods. Excessive foaming was encountered when sheared stainless-clad UO/sub 2/ was suddenly contacted with boiling 13 M nitric acid. While attempting to shear a prototype Yankee subassembly with Kanigan brazed diffusion bonded joints, a five …