Abstract: "The ductility of Type 310 stainless steel T-joints brazed with GE-62 brazing alloy was measured at room temperatures 1200, 1650, and 1800 F. The measure of ductility was taken as the plastic axial strain required to crack braze fillets in T-section tensile specimens. At elevated temperatures, the ductility of as-brazed joints approximated that of the stainless steel, but at room temperature the brazed joints had only one-tenth the ductility of the base metal. Annealing for 16 hr at 1800 F in air was found to triple the room-temperature ductility of the brazed joint."

This report follows a preliminary study on uranium migration in pressed and sintered UO2-bearing bodies based on MoSi2 or Al2O3.

The following report introduces the aquadag, a part of the stellarator with the purposes to prevent the non-uniform accumulation of electrostatic charges on the walls of the stellerator and to free the electrons of the stellerator and provide accelerations, achieving a uniform field distribution.

An improved method for the determination of boron in plutonium is reported. Precipitation of plutonium (III) acid oxalate prior to color development with curcumin results in increased precision, greater speed, and lower costs. Results are presented of a statistical study involving all variables.

Five continuous coatings were produced on zirconium coupons using an anodizing technique. These layers appear to be quite adherent and not subject to visible or audible failure caused by flaxion of the basis metal, Their abrasion resistance, though not investigated thoroughly, appears to be moderately good.