Report presents the correlation of extensive data obtained relating properties of wrought N-155 alloy under static, combined static and dynamic, and complete reversed dynamic stress conditions. Time period for fracture ranged from 50 to 500 hours at room temperature, 1,000 degrees, 1,200 degrees, and 1,500 degrees F.

Flight-test measurements, related analytical studies, and corresponding pilots' opinions of the speed stability of tandem-rotor helicopter are presented. An undesirable instability, evidenced by rearward stick motion with increasing forward speed at constant power, is indicated to be caused by variations with speed of the front-rotor downwash at the rear rotor. An analytical expression for predicting changes in speed stability caused by changes in rotor geometry is derived and constants for use with the analytical expression are presented in chart form. Means for improving stability with speed are studied both analytically and experimentally. The test results also give some information as to the flow conditions at the rear rotor.

From Introduction: "This report extends the short-bearing pressure-distribution function of Michell and Cardullo to give equations for the various bearing characteristics. This short-bearing approximation makes available formulas relating eccentricity ratio to applied load, attitude angle, angular position of peak film pressure to unit pressure on projected area."

This investigation was made to adapt wet-process autoradiography to metallurgical samples to obtain high resolution of segregated radioactive elements in microstructures. Results are confined to development of the technique, which was perfected to a resolution of less than 10 microns. The radioactive samples included carbon-14 carburized iron and steel, nickel-63 electroplated samples, a powder product containing nickel-63, and tungsten-185 in N-155 alloy.