From introduction: This work is a survey of possible uses of ceramic materials in Hanford-type fuel elements.

This report follows a preliminary study on uranium migration in pressed and sintered UO2-bearing bodies based on MoSi2 or Al2O3.

Abstract: "Differential thermal-expansion effects in brazed joints involving Type 310 stainless steel and GE-62 brazing alloy were investigated. The work included dilation and modulus-of-elasticity measurements using homogenous cast specimens and observations on bimetallic cantilevers made of the two constituents. No anomalies were found, although there were irregularities in the expansion of the brazing alloy which were ascribed to a solubility phenomenon. The elastic modulus of the brazing alloy was determined. Cantilever deflections with temperature and with load were measured, and the results were interpreted using equations which treat the specimens as true bimetals consisting of two homogeneous components. The difference in thermal-expansion coefficients obtained in this way from the temperature-deflection data was consistent with the dilation measurements. The load measurements yielded an average elastic modulus for the bimetal which was about two-thirds of what would have been expected from knowledge of the components. This discrepancy probably arose from porosity which was observed in the braze components."