From Summary: "The influence of systematic variations of chemical composition on rupture properties at 1200 degrees F. was determined for 62 modifications of a basic alloy containing 20 percent chromium, 20 percent nickel, 20 percent cobalt, 3 percent molybdenum, 2 percent tungsten, 1 percent columbium, 0.15 percent carbon, 1.7 percent manganese, 0.5 percent silicon, 0.12 percent nitrogen and the balance iron. These modifications included individual variations of each of 10 elements present and simultaneous variations of molybdenum, tungsten, and columbium. Laboratory induction furnace heats were hot-forged to round bar stock, solution-treated at 2200 degrees F., and aged at 1400 degrees F."

A method introduced by Munk is extended to prove that the light-curve slope of thin wings in either subsonic flow or supersonic flow is the same when the direction of flight of the wing is reversed. It is also shown that the wing reversal does not change the thickness drag, damping-in-roll parameter or the damping-in-pitch parameter.