"Short-range order coefficients were measured at 300 and 400°C for iron-aluminum alloys containing 14.8, 18.2, and 20.0 atomic per cent aluminum. These alloys exhibited a strong preference for unlike near neighbors. The short-range order was greater at the lower temperature and increased as the Fe 3Al composition was approached."

"Theoretical calculations have been carried our for the two ordering phases which occur in the FeAl system. The statistical treatment involves first and second neighbor interaction parameters as well as a magnetic interaction between first neighbor iron atoms. The phase diagram and the amount and type of long range order for slowly cooled alloys are calculated. Further calculations include short range order for the disordered phase at three compositions and two temperatures. As expected, the short range order increases as a critical temperature is approached either in composition of in temperature."

"Contact conductances for three semi-smooth and rough stainless steel contacts involving six steels are determined. The procedure and equipment used are fully described, and the results are given. Graphs display thermal conductance and conductivity versus pressure and temperature."

"The behavior of charged particles in a plasma-free cusp field, or in a cusp field where there is very little plasma, is studied. The numerical computations described may provide a valid picture of the behavior of particles outside such a body of plasma or in the early stages of creation of such a cusped plasma in the low- beta limit. The computations provide a striking illustration of orbits which neither have constant magnetic moment nor behave so irregularly as to defy explanation."

"A series of glass compositions containing uranium oxide was investigated to determine fiberizability and physical properties of resultant fibers. The basic properties to be determined were the maximum U/sub 3/O/sub 8/ content in a fiberizable glass and the maximum service temperature of the fibers. Glasses containing 60 wt% U/sub 3/O/sib 8/ were fiberizable; the fibers had strengths of 100,000 psi at 1600 deg F. Fiber-forming equipment was installed at Moun Laboratory to produce glass fibers containing PuO/sub 2/. Fibers were successfully formed in the first trials. For additional work a series of base glasses were provided affording a wider range of both PuO/sub 2/ solubility and physical properties."