Impermeable Thin Al2O3 Overlay for TBC Protection From Sulfate and Vanadate Attack in Gas Turbines Quarterly Report
In order to improve the hot corrosion resistance of conventional YSZ TBC system, a thin and dense {alpha}-Al{sub 2}O{sub 3} overlay has been deposited on the YSZ surface by the composite-sol-gel route (CSG). The YSZ substrates were dipped with boehmite sol containing calcined {alpha}-Al{sub 2}O{sub 3} particles, dried to form a gel film and calcined at 1200 C to form {alpha}-Al{sub 2}O{sub 3} overlay. Hot corrosion tests were carried out on the TBCs with and without Al{sub 2}O{sub 3} coating in molten salt mixtures (Na{sub 2}SO{sub 4} + 5% V{sub 2}O{sub 5}) at 950 C for 10 hours. The results showed that besides a thin and dense alumina overlay with the thickness of about 100-500 nm formed on the YSZ surface, the microcracks and porous near the surface in YSZ was also occupied by alumina because of penetration of the low viscosity precursor. As a result, the Al{sub 2}O{sub 3} overlay remarkably refrained the infiltration of the molten salt into the YSZ coating. The amount of M-phase in the TBC coating with Al{sub 2}O{sub 3} overlay was substantially reduced comparing to that without alumina overlay. In the next reporting period, we will prepare the alumina overlay by CSG route with …
Date:
March 10, 2003
Creator:
Mao, Scott X.
System:
The UNT Digital Library