Diffusion welding is shown to be a feasible method for joining composites of niobium-titanium superconductor alloy filaments in a pure copper matrix. Good results were repeatedly obtained using 15/sup 0/ scarf joints welded with externally heated tooling and simple uniaxial compression loading in a conventional hydraulic press. Weld cycles of less than one hour total elapsed time were readily attainable. Through proper closed-die design, it was possible to increase welding pressure sufficiently to use relatively low temperatures to coincide with the optimum aging heat treatment of the superconductor alloy. This temperature limitation is important to retain optimal superconductor properties. Confirming measurements of critical current density of welded joints at 4.2/sup 0/K are in progress. In the welded joints made under optimum conditions, there is bonding of all constituents, including superconductor filaments. Weld tooling which effectively contains the relatively fluid matrix, and resists deformation during repeated weld cycles, is essential to the successful application of the diffusion welding process to these composites.