An investigation was conducted to study the mechanisms of blade failure of forged Hastelloy B and cast Stellite 21. The blades were mounted in a 16-25-6 alloy rotor and subjected to 20-minute cycles consisting of 15 minutes at rated speed and approximately 5 minutes at idle. The first failures of the Hastelloy B and Stellite 21 blades were probably the result of excessive vibratory stresses and occurred after 14.25 and 16.75 hours, respectively. After 28.75 hours of operation, all but 3 of the original 25 Hastelloy B blades had either failed or contained stress-rupture-type cracks and four of the original 27 Stellite 21 blades contained stress-rupture-type cracks.

Tests have been conducted in the Langley high-speed 7- by 10-foot tunnel over a Mach number range from 0.40 to 0.91 to determine the stability and control characteristics of an 0.08-scale model of the Chance Vought XF7U-1 airplane. The aileron characteristics of the complete model are presented in the present report with a very limited analysis of the results.

From Summary: "Measurements of wing and fuselage pressure distributions were made at low and high subsonic Much numbers on a 0.16-scale model of the projected MX-656 research airplane. The MX-656 is a supersonic design utilizing a low-aspect-ratio wing and tail. Pressure-distribution measurements indicated that, although the critical Mach number of the wing was approximately 0.81 at 0 degree angle of attack, compressibility effects were of little significance below a Mach number of at least 0.90. The principal effect of compressibility was an increase in the pressure gradient over the after 30 percent of the wing chord, causing a tendency for the flow to separate."