The operation of the HRT mockup was on 0.042m UO2SO4, 0.024m H2SO4, and 0.005m CuSO4 at 280 C and 1400 psi pressure. with the O2 content at near 500 ppm. The pump showed bearing wear and high corrosion. The letdown heat exchanger was removed from the mockup and sectioned. The metallographic examination revealed corrosion. Results of corrosion runs on Ti, zircaloy-2, and stainless steel are given.

During the development of in-reactor corrosion experiments three types of bomb designs have been developed for following quantitatively the consumption of oxygen in a bomb which is fabricated from the particular metal under test. The bombs are designed so as to be rocked continuously during their in-reactor exposure, consequently agitating the uranium salt solution contained in the bomb and permitting gentle movement of the solution past metal specimens and other corroding surfaces. The oxygen pressure is produced within the bomb at the beginning of the run either by the withdrawal of gas from an oxygen tank or by the decomposition of hydrogen peroxide added just prior to closure. Temperature measurements are obtained by mans of thermocouples placed in a well within the bomb body or, in the latest design, there will also be thermocouples staked at several points on the outer wall of the bomb. The assembly is inserted in an experimental access hole in the reactor, brought up to a predetermined operating temperature by means of an electric furnace in close contact with the bomb, and allowed to remain for the desired amount of exposure to reactor radiation. Periodic measurements of temperature and pressure are made and the bomb …