Abstract: The question of how crack-free, protective oxide films can form on zirconium during oxidation when the Pilling-Bedworth ratio is about 1.5 has been considered by a study of the relative plasticity of various forms of zirconia. Hot hardness measurements showed that doping mono-clinic zirconia with iron, nickel, or chromium resulted in softer (more plastic) structures and that yttrium additions slightly reduced the plasticity. Calcia-stabilized cubic zirconia was found to be more plastic than mono-clinic zirconia when tested at temperatures above 200 degrees C. The behavior of anion-deficient oxides indicated that they were more plastic than stoichiometric oxides even though the hardness values were identical at 23 degrees C. The former were free from cracks at the indentions, whereas, stoichiometric oxides exhibited extensive cracking around and between indentions. The behavior of actual, thick (72 microns) oxide films during tensile deformation of oxidized metal samples indicated that considerable plasticity occurs in the oxide at 500 degrees C but that the films are brittle at 23 degrees C. It was concluded that the plasticity of the oxide may be greater than that of the oxygen-contaminated substrate at elevated temperatures and may be the means by which epitaxial strains are minimized.

From introductory paragraphs: "The central problems in neutron research are the understanding of nuclear structure and the study of the properties of nuclear particles, particularly the properties of the neutron. The most fruitful attack on these problems is the determination of the probability of interactions between neutrons and nuclei, i.e., the measurement of neutron cross sections. Ideally, this involves the study of all possible types of neutron interaction with all available nuclei at all neutron energies...The discussion in this paper will omit the interactions leading to neutron productions, and will be limited to the intersections of neutrons with stable nuclei."