The following report focuses on an investigation made to determine if vacuum melting was an absolutely necessary step in the metallurgical process of melting and casting uranium.

Abstract: This project was designed to test the chemical feasibility of depositing of depositing a primary uranium mineral from a pregnant solution by exposing the solution to natural gas in an environment favorable to such deposition.

Abstract: This report presents the results of a study performed by the Ford Instrument Company, Division of Sperry Rand Corporation, and its subcontractor, Maryland Shipbuilding & Drydock Company, for the Maritime Administration, U. S. Department of Commerce, under terms of Study Contract No. MA-1893, dated March 11, 1959. The purpose of this study is to evaluate various techniques for pretesting and installing nuclear prototype power plants in merchant ships and develop that technique offering the widest general application using time, cost and safety as essential criteria. Acknowledgement is made for the valuable counsel received from personnel of the American Bureau of Shipping, Isbrandtsen Company, Inc., Maritime Administration, Atomic Energy Commission, and the United States Coast Guard.

Introduction: Studies of uranium-vanadium occurrences in the Four Corners region show that, with the exception of the Lukachuai area, all of the major deposits in the Morrison formation are grouped around the various igneous masses which are scattered irregularly throughout the Colorado Plateau. The pattern of deposition varies from mountain group to mountain group and each will be described separately. Maps accompany this report to supplement the descriptions of ore occurrences in the vicinity of the La Sal, Abajo, Carrizo, and Henry mountains. Elsewhere, it is believed that a written description will suffice.

Technical report containing short reports on (1) Mass spectrometer studies; (2) Purification of heavy water; and (3) Equilibration studies.

Technical report. Numerous application of various column adsorption techniques to inorganic analytical chemistry have appear in the literature. The comparatively recent introduction of ion exchange resins has resulted in the development of efficient, simple, and rapid column adsorption methods. the principal service of column adsorption methods to analytical chemistry is that of providing a relatively simple means of separating an element in a sufficiently pure state so that a direct precipitation, ignition, and weighting, for example, will suffice to complete the quantitative analysis. Systems involving uranyl nitrate will naturally be emphasized in this report but information will be included concerning the separation of the individual members of a series from one another, such as in the alkaline earths and the rare earths.

"Results of tests indicate that the nucerite-bearium seal system is compatible. This combination was operated as long as 9 hours without serious damage. In other work, the test rig was modified to eliminate pressure fluctuations and extraneous dirt, and Type IIA seal parts were designed."

From objectives: This report demonstrates the concept of hydrogeochemical sampling to be used in the 12-state region for which UCC-ND has the responsibility if surveying as part of the NURE. The results of a geochemical survey at two sample spacings in the Crystal City Quadrangle in south Texas are presented.

The results of analyses of the airborne gamma radiation and total magnetic field survey flown for the region identified as the Trona National Topographic Map NI-11-12 is presented in Volume I and II of this report. This volume gives the description of the program and the results.

Abstract: The erroneously high values for uranium content of salvage solutions as determined by the ether extraction-ascorbic acid procedure have been demonstrated to be due to the presence of colored organic materials in these solutions. Evaporation of such solutions to fumes of HC104 before extraction has been shown to be completely successful in preventing such interference while pretreatment with activated carbon is sufficiently successful for application in Control laboratories. Complete procedures for application of either protreatment and results of such application to composite salvage solutions received over a six-month period are included.

The following report provides data that was discovered from a preliminary literature survey that was made to define the utility of the newer refractory ceramics or ceramic-based materials.

The following report analyzes several reported incidents of uranium-rich zirconium-uranium explosions. This report offers notes designed to describe conditions sufficient to cause an explosion with an 80% wt. uranium alloy.

Abstract: "Photographic plates have been used to measure the energy of neutrons from the fission of 25. The spectrum as inferred from the ranges of 850 protons recoiling in the forward direction shows a very wide maximum at ~1.5 Mev with an exponentially decreasing high energy tail which extends beyond 7 Mev. The minimum energy neutrons recorded were ~700 kv. If the spectrum is extrapolated to zero, one finds that this average neutron energy is about 1.85 Mev. The stopping power of the plates was calibrated by the use of monochromatic neutrons from the Li-7(pn) Be-7 reaction and the d-d reaction."

Abstract: "A summary of the contents of numerous reports on the liquid phase proportion of uranium chloride."

The following report describes the welding procedures for welding austenitic stainless steel to carbon steel through a shielded metal-arc process, including the safety precautions and post-production process.

Uranium was plastically deformed 90% at room temperature by unidirectional rolling to a foil 0.002-inches thick. Specimens were recrystallized in the alpha region and several pole figures obtained from 0 to 40 degrees. From these, the preferred orientation was found to be in a spread of idealized (11) [010] about [010].

A program has begun embodying a study of the diffusion rates of krypton and xenon into unirradiated UO2 and UC at temperatures between 1000°C and 2500°C.The experimental technique is described in some detail, involving exposure of UO2 and UC samples to a Kr85 atmosphere at various temperatures, removal of surface-adsorbed krypton, dissolution of the sample, collection and ion chamber measurement of the diffused Kr, and calculation of diffusion coefficients from these data.

Abstract: Pure UO2F2 is made by reaction between anhydrous HF and pure UO3. Although it is difficult to prepare free of water, it is not very hygroscopic. Prolonged heating at 100-105 degrees releases 99.9% of the water in an aqueous solution; the rate of loss of water is very small after saturation is reached. X-ray diffraction data give a density of 6.2 for the solid. The density of a 1.004 M solution is 1.274; the density of a saturated solution (5.130 M) is 2.400. The densities of F-9 solutions have been calculated from the densities of ordinary aqueous solutions, and the values are compared graphically. Data on the solubility indicate that there is a small increase in the range 25-100 degrees. Recovery of pure F-9 from a solution is hampered by hydrolysis of U)2F2 to give HF. The HF may be held back by addition of UO3 or CaO; the use of the latter, however, makes more difficult the recovery of all the F-9. Molar conductivities of UO2F2 solutions at 25 degrees, as well as the specific conductivities of a 1 molar solution containing various concentrations of UO3, have been determined. The addition of UO3 lowers the conductivity. The low …

"The possibility of radioactivity transport in the groundwater system as the result of a hypothetical maximum credible gas leak was evaluated." "The present study confirms the low radiation levels in the groundwater predicted in the initial calculations." (from Summary)

Data collected as part of a uranium geochemical survey in the Crystal City and Beeville Quadrangles in Texas including laboratory data stream sediments and water, well water, and botanical samples for phase 1 (pp. 1-8); for phase 2 including the same with lake samples (pp 9-36); well water samples only for phase G (p. 37); and field data for all phases (pp. 38-374).

A method to determine the correction to Grüneisen's law corresponding to the effect of the electrons at high pressure. It is assumed that the lattice contribution to the pressure is small and that the equation of state of the solid can be approximated by results of the statistical Thomas-Fermi atom model for the electron pressure.

The object of this project is to conduct studies on the coating of metals and alloys by the gas plating process. Coatings to be studied consist of chromium on copper; alloys of nickel chromium on copper; molybdenum on stainless steel and Inconel; chromium on stainless steel and Inconel; and tungsten and molybdenum and their carbides on stainless steel and Inconel.

Single record data listings taken during aerial gamma-ray and magnetic surveys of the Trona quadrangle in California.

Average record data listings taken during aerial gamma-ray and magnetic surveys of the Trona quadrangle in California.