Technical report describing the investigation of the short-lived activities produced in oxygen compounds by irradiation with pile neutrons. The most prominent of these activities in cooling water is a beta and gamma emitting activity of about 8 second half-life. Because of its production by epicadmium neutrons it was believed to be the 8 second N16 produced in the pile by n,p on O16. The identification has been accomplished and it is established that the 8 second activity is N16. Part 2 of the report deals with the determination of the recoil range of the Al28 atoms formed by pile n,p reaction on Al27.

Technical report. Photomicrographs showing the effect of heating polished uranium surface at 600, 700, 850, and 1000 degrees C, and sandblasted and cut surface at 1000 degrees C are included.

.Technical report describing the transference experiments. The carrying of zirconium and columbium by ferric hydroxide has a very marked dependence on pH. In the experiments it was noticed that the concentration of Zr activity in various solutions changed with time This indicated that the Zr was being adsorbed on the glass. The carrier free trace is adsorbed on glass. This effect must be considered in experiments with Zr tracer in glass apparatus.

Abstract. It has been established that heating samples of graphite during exposure in a pile decreases substantially the observed changes in the elastic modulus and electrical resistance caused by the irradiation. The functional relationship between the percentage changes observed and the temperature of exposure resembles the relationship between the final percentage changes and the temperature of heat treatment after exposure (cf. report CC-1668). Anomalous results reported previously for higher temperatures in CC01669 are now shown to be attributable to a destructive influence on the graphite, probably oxidation of samples exposed in air.