Amorphous materials are used as soft magnetic materials and also as surface coatings to improve the surface properties. Furthermore, the nanocrystalline materials derived from their amorphous precursors show superior soft magnetic properties than amorphous counter parts for transformer core applications. In the present work, laser based processing of amorphous materials will be presented. Conventionally, the nanocrystalline materials are synthesized by furnace heat treatment of amorphous precursors. Fe-based amorphous/nanocrystalline materials due to their low cost and superior magnetic properties are the most widely used soft magnetic materials. However, achieving nanocrystalline microstructure in Fe-Si-B ternary system becomes very difficult owing its rapid growth rate at higher temperatures and sluggish diffusion at low temperature annealing. Hence, nanocrystallization in this system is achieved by using alloying additions (Cu and Nb) in the ternary Fe-Si-B system. Thus, increasing the cost and also resulting in reduction of saturation magnetization. laser processing technique is used to achieve extremely fine nanocrystalline microstructure in Fe-Si-B amorphous precursor. Microstructure-magnetic Property-laser processing co-relationship has been established for Fe-Si-B ternary system using analytical techniques. Laser processing improved the magnetic properties with significant increase in saturation magnetization and near zero coercivity values. Amorphous materials exhibit excellent corrosion resistance by virtue of their atomic …

In this dissertation, small and large NaCl particle-derived surfaces (Ra > 40 microns) were generated on 2D Zn materials, and the surfaces were carefully studied concerning topography, corrosion behavior, and bone cell compatibility. Increases in surface roughness accelerated the corrosion rate, and cell viability was maintained. This method was then extended to 3D porous scaffolds prepared by a hybrid AM/casting technique. The scaffolds displayed a near-net shape, an interconnected pore structure, increasing porosity paralleled to an increased corrosion rate, an ability to support cell growth, and powerful antibacterial properties. Lastly, nano/micro (Rz 0.02–1 microns) topographies were generated on 2D Zn materials, and the materials were comprehensively studied with special attention devoted to corrosion behavior, biocompatibility, osteogenic differentiation, immune cell response, hemocompatibility, and antibacterial performance. For the first time, the textured nonhemolytic surfaces on Zn were shown to direct cell fate, and the micro-textures promoted bone cell differentiation and directed immune cells away from an inflammatory phenotype.

Shape memory alloys (SMAs) represent a revolutionary class of active materials that can spontaneously generate strain based on an environmental input, such as temperature or stress. SMAs can provide potential solutions to many of today's engineering problems due to their compact form, high energy densities, and multifunctional capabilities. While many applications in the biomedical, aerospace, automotive, and defense industries have already been investigated and realized for nickel-titanium (NiTi) based SMAs, the effects of controlling and designing the microstructure through processing (i.e. extreme cold working) have not been well understood. Current Ni-Ti based SMAs could be improved upon by increasing their work output, improving dimensional stability, preventing accidental actuation, and reducing strain localization. Additionally, there is a strong need to increase the transformation temperature above 115 °C, the current limit for NiTi and is especially important for aerospace applications. Previous research has shown that the addition on ternary elements such as Au, Hf, Pd, Pt, and Zr to NiTi can greatly increase these transformation temperatures. However, there are several limiting factors with these ternary additions such as increased cost, especially with Au, Pd, and Pt, as well as, difficulty in conventionally processing these alloys. Therefore, the main objectives of this research …

In this work, wear and scratch behavior of four different bulk metallic glasses (BMGs) namely Zr41.2Cu12.5Ni10Ti13.8Be22.5 (LM 1), Zr57Cu15.4Ni12.6Al10Nb5 (LM 106), Ni60Pd20P17B3 (Ni-BMG), and Pt57.5Cu14.7Ni5.3P22.5 (Pt-BMG) were compared. Shear band formation on the edges of the scratch groove with spallation was found to be the primary failure mechanism in progressive scratch tests. The wear behavior and the scratch response of model binary Ni-P metallic glasses was systematically studied as a function of composition, with amorphous alloy formation over the narrow range of 10 at% to 20 at% phosphorus. Pulsed current electrodeposition was used to obtain these binary amorphous alloys, which offers a facile and versatile alternative to conventional melt quenching route. The electrodeposited metallic glasses (EMGs) showed hardness values in the range of 6.6-7.4 GPa, modulus in the range of 155-163 GPa, and friction coefficient around 0.50. Among the studied alloys, electrodeposited Ni80P20 showed the lowest wear rate. The wear mechanism was determined to be extensive plastic deformation along with mild ploughing, micro tears, and formation of discontinuous lubricious oxide patches. The effect of phosphorus content on the structure, mechanical properties, and the tribological response was systematically investigated for biocompatible Co-P metallic glasses. With increase in phosphorus content, there was …

The results from this study, on a few commercial and model metastable beta titanium alloys, indicate that the growth restriction factor (GRF) model fails to interpret the grain growth behavior in the additively manufactured alloys. In lieu of this, an approach based on the classical nucleation theory of solidification incorporating the freezing range has been proposed for the first time to rationalize the experimental observations. Beta titanium alloys with a larger solidification range (liquidus minus solidus temperature) exhibited a more equiaxed grain morphology, while those with smaller solidification ranges exhibited columnar grains. Subsequently, the printability of two candidate beta titanium alloys containing eutectoid elements (Fe) that are prone to beta fleck in conventional casting, i.e., Ti-1Al-8V-5Fe (wt%) or Ti-185, and Ti-10V-2Fe-3Al (wt%) or Ti-10-2-3, is further investigated via two different AM processing routes. These alloys are used for high-strength applications in the aerospace industry, such as landing gears and fasteners. The Laser Engineered Net Shaping and Selective Laser Melting (the two AM techniques) results show that locally higher solidification rates in AM can prevent the problem of beta fleck and potentially produce β-titanium alloys with significantly enhanced mechanical properties over conventionally cast/forged counterparts. Further, the detailed investigation of microstructure-mechanical property …

This work identifies alloy terminal freezing range, columnar growth, grain coarsening, liquid availability towards the terminal stage of solidification, and segregation towards boundaries as primary factors affecting the hot-cracking susceptibility of fusion-based additive manufacturing (F-BAM) processed alloys. Additionally, an integrated computational materials engineering (ICME)-based approach has been formulated to design novel Al alloys, and high entropy alloys for F-BAM processing. The ICME-based approach has led to heterogeneous nucleation-induced grain refinement, terminal eutectic solidification-enabled liquid availability, and segregation-induced coalescence of solidification boundaries during laser-powder bed fusion (L-PBF) processing. In addition to exhibiting a wide crack-free L-PBF processing window, the designed alloys exhibited microstructural heterogeneity and hierarchy (MHH), and thus could leverage the unique process dynamics of L-PBF to produce a fine-tunable MHH and mechanical behavior. Furthermore, alloy chemistry-based fine tuning of the stacking fault energy has led to transformative damage tolerant alloys. Such alloys can shield defects stemming from the stochastic powder bed in L-PBF, and consequently can prevent catastrophic failure despite the solidification defects. A modified materials systems approach that explicitly includes alloy chemistry as a means to modify the printability, properties and performance with F-BAM is also presented. Overall, this work is expected to facilitate application specific manufacture with …

In this study, the time-dependent deformation behavior of several model bulk metallic glasses (BMGs) was studied. The BMGs were obtained in different structural states by thermal relaxation below their glass transition temperature, cryogenic thermal cycling, and chemical rejuvenation by micro-alloying. The creep behavior of Zr52.5Ti5Cu17.9Ni14.6Al10 BMG in different structural states was investigated as a function of peak load and temperature. The creep strain rate sensitivity (SRS) indicated a transition from shear transformation zone (STZ) mediated deformation at room temperature to diffusion dominated mechanisms at high temperatures. The relaxation enthalpy of Zr47Cu46Al7 BMG was found to increase significantly with the addition of 1 at% Ti, namely for Zr47Cu45Al7Ti1. Comparison of their respective free volumes indicated that chemical rejuvenation had a more pronounced effect compared to cryogenic thermal rejuvenation. Micro-pillar compression tests supported the improved plasticity with increase in free volume from the rejuvenation effect. Effect of chemistry change on mechanical response and time-dependent deformation was investigated for topologically equivalent Pt-Pd BMGs, where the Pt atoms were systematically replaced with Pd atoms (Pt42.5-xPdx)Cu27Ni9.5P21: x=0, 7.5, 20, 22.5, 35, 42.5). The hardness and reduced modulus increased while the degree of plasticity decreased with increase in Pd-content, which was attributed to the increase in …

Magnetic field-assisted freeze-casting was used to create porous B4C ceramic preforms. An optimum slurry consisted of a mixture of B4C powders with 6 wt.% Er2O3 powder in an H2O-PVA solution and was cooled at a rate of 1 °C/min from room temperature to -30 °C resulting in porous green state ceramic preform with vertical channels. The Er2O3 powder was added to improve the magnetic response of the slurry. The preform was then sublimated to remove H2O and then sintered. The sintered ceramic preform was then infiltrated in the most vertically aligned channel direction with molten Al (A356) metal through a vacuum-assisted pump to create the metal matrix composite (MMC). Finite element analysis simulations were used to analyze and predict the anisotropic effect of B4C channel alignment on mechanical properties. The mechanical properties of the composite were then experimentally found via compression testing, which was compared with rule-of-mixtures and finite element modeling simulations, to analyze the effect of anisotropy due to magnetic field-assisted freeze-casting. This study reinforces the viability of cost-effective magnetic field-assisted freeze-casting as a method to create highly directional ceramic preforms, which can be subsequently metal infiltrated to produce MMCs with highly anisotropic toughness.

In this work, we have explored 2D semiconducting transition metal dichalcogenides (TMDs), black phosphorus (BP), and graphene for various applications using liquid and mechanical exfoliation routes. The topical areas of interest that motivate our work include considering factors such as device integration, stability, doping, and the effect of gasses to modulate the electronic transport characteristics of the underlying 2D materials. In the first area, we have integrated solution-processed transparent conducting oxides (TCOs), specifically indium-doped tin oxide (ITO) with BP, which is a commonly used TCO for solar cell devices. Here we have found surface treatment of glass substrates with a plasma before spin-coating the solution-processed ITO, to be effective in improving coverage and uniformity of the ITO film by promoting wettability and film adhesion. The maximum transmittance obtained was measured to be ~75% in the visible region, while electrical measurements made on BP/ITO heterostructures showed improved transport characteristics compared to the bare ITO film. Within the integration realm, inkjet-printing of BP and MoS2 p-n hetero-junctions on standard ITO glass substrates in a vertical architecture was also demonstrated. To address the issue of stability which some 2D materials such as BP face, we experimented with ionic liquids (ILs) to passivation the …

Although markets for alternative batteries, such as Li-ion, are growing, Pb-alloy batteries still dominate the market due to their low cost and good functionality. Even though these Pb-alloy batteries have been around since their discovery in 1859, little research involving advanced characterization techniques, such as synchrotron radiation X-ray diffraction (SR-XRD) and transmission electron diffraction (TEM) have been performed on Pb-alloys and sulfation, a failure mode in lead acid batteries, with regards to thermally- and electrochemically-induced changes at the atomic and microstructural scale. Therefore, there is a need to close this scientific gap between research and the application of Pb-alloy battery material. The main objectives of this research are to examine the process of sulfation and its growth mechanisms as well as to study the effects of minor alloying additions in Pb-alloy material. In the first case, nucleation and growth mechanisms of PbSO4 nano- and micro-particles in various solutions are examined using TEM to potentially reduce or control the buildup of PbSO4 on battery electrodes over time. The time dependency of particle morphology was observed using various reaction conditions. This insight can provide avenues to reduce unwanted buildup of PbSO4 on battery electrodes over time which can extend battery life and …

High entropy alloys (HEAs) or complex concentrated alloys (CCAs) represent a new paradigm in structural alloy design. Molten salt corrosion behavior was studied for single-phase HEAs such as TaTiVWZr and HfTaTiVZr, and multi-phase HEAs such as AlCoCrFeNi2.1. De-alloying with porosity formation along the exposed surface and fluxing of unstable oxides were found to be primary corrosion mechanisms. Potentiodynamic polarization study was combined with systematic mass–loss study for TaTiVWZr, HfTaTiVZr, and AlCoCrFeNi2.1 as a function of temperature. Electrochemical impedance spectroscopy (EIS) was used for monitoring the corrosion of TaTiVWZr and HfTaTiVZr in molten fluoride salt at 650 oC. TaTiVWZr and AlCoCrFeNi2.1 showed low corrosion rate in the range of 5.5-7.5 mm/year and low mass-loss in the range of 35-40 mg/cm2 in molten chloride salt at 650 oC. Both TaTiVWZr and HfTaTiVZr showed similar mass loss in the range of 31-33 mg/cm2, which was slightly higher than IN 718 (~ 28 mg/cm2) in molten fluoride salt at 650 oC. Ta-W rich dendrite region in TaTiVWZr showed higher corrosion resistance against dissolution of alloying elements in the molten salt environment. AlCoCrFeNi2.1 showed higher resistance to galvanic corrosion compared to Duplex steel 2205 in molten chloride salt environment. These results suggest the potential use …

Asymmetric polymeric materials can be formed by either top-down or bottom-up methods. Bottom-up methods involve assembling the atoms and molecules to form small nanostructures by carefully controlled synthesis, which results in a reduction of some of the top-down limitations. In this dissertation, thermal, tribological and antireflective properties of polymeric materials have been enhanced by introducing structural asymmetry. The overall performance of commercial polymeric coatings, e.g. epoxy and polyvinyl chloride, has been improved by conducting the blending methods, specifically, chemical modification (α,ω-dihydroxydimethyl(methyl-vinyl)oligoorganosiloxane), cross-linking (triallyl isocyanurate), and antioxidant (tris(nonylphenyl) phosphite) incorporation. The nonequilibrium polymeric structures (moth-eye and square array) have been developed for the ultrahigh molecular weight block copolymers via the short-term solvent vapor annealing self-assembly. The large domain size of the moth eye structure allows for improvement of the light transmittance particularly in the visible and near infrared ranges, while the square arrangement of the block copolymer opens the possibility of magnetic data storage application by the large magnetic nanoparticles' embedment or masking of the superconductors.

To minimize global carbon emissions, having efficient jet engines and internal combustion engines necessitates utilizing lightweight alloys such as Al, Ti, and Mg-based alloys. Because of their remarkable strength/weight ratio, these alloys have received a lot of attention. Nonetheless, they have very poor tribological behavior, particularly at elevated temperatures beyond 200 °C, when most liquid lubricants begin to fail in lubrication. Over the last two decades, there has been a lot of interest in protecting Al, and Ti-based alloys by developing multiphase solid lubricants with a hard sublayer that provide mechanical strength and maintain the part's integrity while providing lubricity. The development of novel coatings with superior lubricity, high toughness, and high-temperature tolerance remains a challenging and hot topic to research and provide new engineered solutions for. To address and provide solutions to protect light-weight, i.e., Al, and Ti alloys at high-temperature and bestow superior tribological properties to such alloys, three types of adaptive lubricious coatings have been studied in this thesis: Nb-Ag-O self-healing lubricious ternary oxide, PEO-chameleon a self-adaptive multi-phase coating, and Sb2O3-MSH-C lubricious adaptive coatings to address this challenge. The development of the Nb-Ag-O ternary resulted in a coefficient of friction as low as 0.2 at 600 °C …

Complex concentrated alloys (CCAs) offer the unique ability to tune composition and microstructure to achieve a wide range of mechanical performance. Recently, the development of metastable CCAs has led to the creation of transformation-induced plasticity (TRIP) CCAs. Similar to TRIP steels, TRIP CCAs are more effective at absorbing high strain rate loads when TRIP is activated during the loading process. The objective of our study is to investigate the effect of copper on the critical pressure for activating TRIP and the high pressure stability of a Fe(40-X)Mn20Cr15Co20Si5CuX TRIP CCA, where x varies from 0 to 3 at.% Cu. To achieve this goal, diamond anvil cell testing during in-situ synchrotron radiation X-ray diffraction was performed using both a monochromatic wide angle X-ray scattering (WAXS) beam and, for the first time ever, a polychromatic Laue diffraction beam on a CCA. Laue diffraction allows for real-time phase evolution tracking of the γ-fcc → ε-hcp transformation in a high pressure environment. Based on the results, a new method for processing and preparation of high pressure samples without changing the microstructure of sample was developed. This new method can be used to prepare any CCA samples for high pressure testing.

Bioactive glass is a type of third generation bioactive material that can bond to both soft and hard tissue with applications ranging from bone defect repair, coatings for metallic implants, to scaffolds for tissue engineering. Design of bioactive glasses for these applications rely on a detailed understanding of the structures of these glasses which are complicated and multicomponent. In this thesis, I have applied molecular dynamics (MD) simulations with interatomic potentials developed in our group to understand the effect of modifier cation substitution on the structures and properties of two series of bioactive glasses. Particularly, MD simulations are used to understand K2O to Na2O and MgO to CaO substitution on the short and medium range structures (such as cation coordination number, pair distribution function, Qn distribution, and ring size distribution) and properties (such as bulk and Young's moduli and CTE) of 55S4.1 bioactive glasses. As Na2O is incrementally substituted with K2O in 55S4.1, a decrease of the glass transition temperature (Tg) and an increase of CTE was observed, as well as a decreasing trend in the moduli. For the MgO to CaO substitution series, Mg2+ is mainly four-fold coordinated that suggests that it can play a role as a network …

The design and fabrication of porous ceramic materials with anisotropic properties has, in recent years, gained popularity due to their potential application in various areas that include medical, energy, defense, space, and aerospace. Freeze-casting is an effective, low-cost, and safe method as a wet shaping technique to create these structures. To control the morphology of these materials, many critical factors were found to play an important role. In this dissertation, the processing parameters of the magnetic field-assisted freeze-casting method were optimized with a focus on comparing the structure obtained using vertical and horizontal magnetic fields and understanding the mechanisms that occur under different freezing modes. More specifically, this processing method was used to produce Al2O3 and B4C porous ceramics materials with unidirectionally-aligned pore channels. The effect of the vertical and horizontal magnetic field strength and direction, concentration of magnetic material (Fe3O4), cooling rate, and freezing time were examined. The resulting ceramics with highly aligned pore channels were infiltrated with molten metal to create metal matrix composites. The mechanical properties of these structures were measured and were subsequently correlated to their morphology and composition.

This dissertation presents an assortment of research aimed at understanding the composition-dependence of deformation behavior and the response to thermomechanical processing, to enable efficient design and processing of low stacking fault energy (SFE) high entropy alloy (HEAs). The deformation behavior and SFE of four low SFE HEAs were predicted and experimentally verified using electron microscopy and in-situ neutron diffraction. A new approach of employing a minimization function to refine and improve the accuracy of a semi-empirically derived expression relating composition with SFE is demonstrated. Ultimately, by employing the minimization function, the average difference between experimental and predicted SFE was found to be 2.64 mJ m-2. Benchmarking with currently available approaches suggests that integrating minimization functions can substantially improve prediction accuracy and promote efficient HEA design with expansion of databases. Additionally, in-situ neutron diffraction was used to present the first in-situ measurement of the interspacing between stacking faults (SFs) which were correlated with work hardening behavior. Electron transparent specimens (< ~100 nm thick) were used in order to resolve nanoscale planar faults instead of the thicker sub-sized specimens (on the order of millimeters in thickness) which exhibit the classical stages III work hardening behavior characteristic of low SFE metals and alloys. …