This thesis is a study of the structural, electrical and magnetic properties of indium antimonide (InSb) nanowires (NWs), that were synthesized by a template-assisted ordered growth technique via electrochemical deposition. InSb was chosen for this study because of its intrinsic properties that make it a material of choice for applications in high channel mobility, infrared (IR) sensing, thermoelectrics, and magnetoresistive sensing martials. This work has four main components: (i) Growth in commercially available anodic aluminum oxide (AAO) template, where hole-dominated conduction was observed, following NW growth in a low pH electrolyte. The challenge in using these AAO templates was in covering the back surface of the pores with a metal film. Uncovered pores resulted in electrolyte leakage and non-reproducible results. (ii) Growth in flexible polycarbonate membranes, where the flexibility of the membranes resulted in polycrystalline or high defect density NW growth. (iii) Fabrication of an AAO template, where the barrier layer thinning technique was found to be efficient in removal of the think aluminum oxide barrier that exists at the interface between the template and the aluminum metal. This allows for direct growth of NWs into the template pores without the need for metal evaporation. (iv) Fabrication of a heterostructure …

The aim of this thesis is to develop both Yb and Tm fiber laser sources with all fiber cavities. Both wavelength ranges provide useful laser sources for optical pumping of helium. The goal is to develop Tm laser sources operating at 2058 nm to optically quench 3He (2058.63 nm) and 4He (2058.69 nm) singlets (21S0). We also have developed Yb laser sources at 1083 nm to optical pump the triplet states of helium and laser cool an atomic beam of helium.

In this dissertation, we study the optical property of 2D graded photonic super-crystals (GPSCs) for photon management. We focused primarily on manipulation and control of light by using the newly discovered GPSCs which present great opportunity for electromagnetic wave control in photonic devices. The GPSC has been used to explore the superior capability of improving the light extraction efficiency of OLEDs. The enhancement of extraction efficiency has been explained in term of destructive interference of surface plasmon resonance and out-coupling of surface plasmon through phase matching provided by GPSC and verified by e-field intensity distributions. A large light extraction efficiency up to 75% into glass substrate has been predicted through simulation. We also study the light trapping enhancement in GPSCs. Broadband, wide incident angle, and polarization independent light trapping enhancement is achieved in silicon solar cells patterned with the GPSCs. In addition, novel 2D GPSCs were fabricated using holographic lithography through the interference lithography by two sets of multiple beams arranged in a cone geometry using a spatial light modulator (SLM). Finally, we also report a fabrication of GPSCs with a super-cell size of 12a×12a by using e-beam lithography. Diffraction pattern from GPSCs reveals unique diffraction properties. In an application …

Silicates analogous to cosmic dust were synthesized, modified, and analyzed utilizing ion-beam techniques with Rutherford backscattering spectrometry (RBS) and x-ray diffraction (XRD). Silicate dust is a common constituent in interstellar space, with an estimated 50% of dust produced in the stellar winds of M class Asymptotic Giant Branch (AGB) stars. Silicate dust acts as a surface upon which other chemicals may form (water ice for example), increasing significance in the cosmochemistry field, as well as laboratory astrophysics. Silicate formation in the stellar winds of AGB stars was simulated in the laboratory environment. Three sequential ion implantations of Fe-, MgH2-, and O- with thermal annealing were used to synthesize a mixture appropriate to silicate dust in the surface layers of a p-type Si substrate. Post implantation He+ irradiation was shown to preferentially induce crystalline formation in the analogue prior to thermal annealing. This effect is believed to originate in the ion-electron interaction in the Si substrate. The effects of ionization and ion energy loss due to electronic stopping forces is believed to precipitate nucleation in the amorphous media. For annealing temperatures of 1273 K, predominant quartz formation was found in the substrate, whereas lower annealing temperatures of 1000 K formed enstatite …