Extrusion was run on one day, February 2, and a total of 271 billets (178 Type G, 12 type BT, and 81 red band) were processed. Two failures occurred among the red band billets; UM 6610 had begun to melt in the furnace and TX 3323 disintegrated on being extruded through the die. Samples of these billets are being checked chemically and metallurgically in an attempt to ascertain the cause for the hot-short characteristics of these billets. A sample cut from a rod which possessed zero strength (fell apart under no stress other than its own weight) at extrusion temperature was found to contain a large amount of microconstituent not ordinarily found in appreciable quantity on uranium sections. The distribution and appearance of the excess phase suggested at least partial liquation at the working temperature and it could, therefore, be responsible for the hot-short tendency.

The attenuation of electro-statically and electro-magnetically shielded rooms in the ``E,`` ``R,`` ``I,`` and ``T`` Buildings was measured so that corrective measure could be taken if the attenuation was found to be low. If remedial measures could not be taken, the shortcomings of the rooms would be known. Also, the men making the measurements should oversee construction and correct errors at the time. The work was performed by measuring the attenuation at spot frequencies over the range of from 150 kilocycles to 1280 megacycles with suitable equipment mounted in small rubber-tried trucks. The attenuation was determined by ``before and after`` shielding and/or ``door open and door closed`` measurements after installation of copper shielding. In general, attenuation in the frequency range of approximately 10 to 150 mc. was good and was of the order expected. At frequencies in the range of 150 mc. to 1280 mc., the attenuation curve was more erratic; that is, at certain frequencies a severe loss of attenuation was noted, while at others, the attenuation was very good. This was mainly due to poor or faulty seals around doors and pass windows. These poor seals existed in the ``T,`` ``E,`` and ``I`` Buildings because the doors were …