Abstract: "Sound, fabricable ingots of thorium were produced by triple are melting of electrolytic thorium. Consumable electrodes were fabricated by tack welding of cold-pressed and vacuum-sintered bars of the granular thorium electrodeposited from a molten-salt bath. The hydrogen content of the electrodeposited material was reduced from 80 to 4 ppm by vacuum sintering at 1250 C at pressures below 1 x 10-(-3) mm of mercury. Both sodium and chlorine content were reduced during melting; sodium from 250 to 25 ppm and chlorine from 1000 to 30 ppm. Oxygen and HCl acid-insoluble contents increased during sintering and melting. Oxygen content increased from 0.35 to 0.50 w/o and HCl acid-insoluble content from 0.8 to 4.0 w/o. A starlike includion revealed by metallographic examination of the as-cast thorium was identified as ThO2."