"A set of dimpling tools was designed for 0.040-inch 24S-T sheet and flush-type rivets 1/8 inch in diameter with 100 degree countersunk heads. The dimples produced under different conditions of pressure, sheet thickness, and drill diameter are presented as cross-sectional photographs magnified 20 times. The most satisfactory values for the dimpling tools were found to be: maximum punch diameter, 0.231 inch; maximum die diameter, 0.223 inch; maximum mandrel diameter, 0.128 inch; dimple angle, 100 degree; punch springback angle, 1 1/2 degree; and die springback angle, 2 degree" (p. 1).

"A graphical method is described for finding the shape (camber and twist) of an airfoil having an arbitrary distribution of lift. The method consists in replacing the lifting surface and its wake with an equivalent arrangement of vortices and in finding the associated vertical velocities. By a division of the vortex pattern into circular strips concentric about the downwash point instead of into the usual rectangular strips, the lifting surface is reduced for each downwash point to an equivalent loaded line for which the induced velocity is readily computed" (p. 1).

Report presenting testing of eighteen 24S-T aluminum alloy sheet-stringer panels in end compression under carefully controlled edge conditions. Results regarding the strains, deflections, failure, and buckling of the sheet are provided.

"Fatigue tests were made on some 1.375-inch-diameter and 0.300-inch diameter specimens of a 17S-T aluminum alloy rod. One test of a large specimen was run continuously to failure at a maximum stress of 22,000 pounds per square inch. In two other tests of large specimens, thin surface layers were removed periodically until failure occurred. The same nominal maximum stress of 22,000 pounds per square inch was used throughout the two tests and the load on the fatigue machine was lowered accordingly after the removal of each surface layer" (p. 1).

From Summary: "A 1/6-full-size model of the hull of the British Singapore IIC flying boat was tested in the NACA tank. The results are given in the form of charts and are compared with the results of previous tests made in the NACA tank of a 1/12-full-size model, published in NACA T.N. No. 580, and with the results of tests made in the British R.A.E. tank of another 1/6-full-size model of the same hull. When the data from the tests of the 1/6- and 1/12-full-size models were compared on the basis of Froude's law of comparison, differences were found."