Ruthenium and ruthenium dioxide thin films have shown great promise in various applications, such as thick film resistors, buffer layers for yttrium barium copper oxide (YBCO) superconducting thin films, and as electrodes in ferroelectric memories. Other potential applications in Si based complementary metal oxide semiconductor (CMOS) devices are currently being studied. The search for alternative metal-based gate electrodes as a replacement of poly-Si gates has intensified during the last few years. Metal gates are required to maintain scaling and performance of future CMOS devices. Ru based materials have many desirable properties and are good gate electrode candidates for future metal-oxide-semiconductor (MOS) device applications. Moreover, Ru and RuO2 are promising candidates as diffusion barriers for copper interconnects. In this thesis, the thermal stability and interfacial diffusion and reaction of both Ru and RuO2 thin films on HfO2 gate dielectrics were investigated using Rutherford backscattering spectrometry (RBS), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). An overview of Ru and RuO2/HfO2 interface integrity issues will be presented. In addition, the effects of C ion modification of RuO2 thin films on the physico-chemical and electrical properties are evaluated.

This problem in lieu of thesis report presents a study on gate electrode materials on high K dielectrics, including poly-SiGe and Ru. The stability of poly-SiGe in direct contact with Hf silicon-oxynitride (HfSiON) is studied by rapid thermal annealing (RTA), Rutherford backscattering spectrometry (RBS), X-ray photoelectron spectroscopy (XPS) and high resolution transmission electron microscopy (HRTEM). By performing a series of RTA treatments we found that as RTA thermal budgets reach 1050 C for 30s, the poly-SiGe layer begins to intermix with the HfSiON film, as observed by TEM. The maximum annealing condition for the Hf0.14Si0.23O0.46N0.17 film to remain stable in contact with poly-SiGe is 1050 C for 20s in high purity N2(99.9%) ambient. We also found that after 1000 C annealing for 60s in a nitrogen ambient, the poly-SiGe crystal phase structure was changed from a columnar structure to a large grain structure. For a metal gate, Ru was studied to determine N2annealing effects on sheet resistance of Ru sample electrodes and electrical characterization of Ru/HfSiOx/Si stack. Results show that a pure Ru metal gate is not a good choice for high k materials since it is hard to etch off, and different annealing conditions can cause large changes in …