There is a high demand for the development of processes for the conversion of ubiquitous molecules into industrially useful commodities. Transition metal catalysts are often utilized for the activation and functionalization of small organic molecules due to their diverse nature and proven utility with a myriad of chemical transformations. The functionalization of methane (CH4) and dinitrogen (N2) to methanol (CH3OH) and ammonia (NH3) respectively is of particular interest; however, both methane and dinitrogen are essentially inert due to the inherit strength of their bonds. In this dissertation a series of computational studies is performed to better understand the fundamental chemistry behind the functionalization of methane and the activation of dinitrogen in a homogeneous environment. A catalytic cycle is proposed for the oxy-functionalization of methane to methanol. The cycle consists of two key steps: (1) C-H activation across a metal-alkoxide bond (M-OR), and (2) regeneration of the M-OR species through an oxy-insertion step utilizing external oxidants. The C-H activation step has been extensively studied; however, the latter step is not as well understood with limited examples. For this work, we focus on the oxy-insertion step starting with a class of compounds known to do C-H activation (i.e., Pt(II) systems). Computational studies …

Zinc-nickel ?-phase silicate and copper-nickel silicate corrosion resistant coatings have been prepared via electrochemical methods to improve currently available corrosion resistant materials in the oil and gas industry. A layered silicate, montmorillonite, has been incorporated into the coatings for increased corrosion protection. For the zinc nickel silicate coatings, optimal plating conditions were determined to be a working pH range of 9.3 -9.5 with a borate based electrolyte solution, resulting in more uniform deposits and better corrosion protection of the basis metal as compared to acidic conditions. Quality, strongly adhering deposits were obtained quickly with strong, even overall coverage of the metal substrate. The corrosion current of the zinc-nickel-silicate coating is Icorr = 3.33E-6 for a borate based bath as compared to a zinc-nickel bath without silicate incorporation (Icorr = 3.52E-5). Step potential and direct potential methods were examined, showing a morphological advantage to step potential deposition. The effect of borate addition was examined in relation to zinc, nickel and zinc-nickel alloy deposition. Borate was found to affect the onset of hydrogen evolution and was examined for absorption onto the electrode surface. For copper-nickel silicate coatings, optimal conditions were determined to be a citrate based electrolytic bath, with pH = 6. …