"Centrifugal-casting techniques were investigated as a method of producing hollow cylindrical extrusion billets of aluminum-35 w/o uranium. Among the variables evaluated were melt temperature, mold and pouring-spout configurations, mold speed, and method of pouring. With the equipment employed it was found that the best castings were produced stilizing a pouring temperature of 2400 F, a heavy-walled steel cylinder rotating between 700 to 900 rpm for the mold and bottom-pouring technique employing a retractable pouring spout. Sound, nonporous billets 26 in. long and 5 in. in diameter were produced with a yield after machining of over 75 per cent of the original charge. The major losses occurred in the pouring spout-and-cup assembly. This loss is relatively unaffected by the casting length; and, therefore, coatings of greater length than 26 in. should results in even greater recoveries.

Centrifugal-casting techniques were investigated as a method of producing hollow cylindrical extrusion billets of aluminum-35 wt.% uranium. Among the variables evaluated were melt temperature, mold and pouring-spout configurations, mold speed, and method of pouring. With the equipment employed it was found that the best castings were produced utilizing a pouring temperature of 2400 ction prod- , a heavy-walled steel cylinder rotating between 700 and 900 rpm for the mold and a bottom-pouring technique employing a retractable pouring spout. Sound, nonporous billets 26 in. long and 5 in. in diameter were produced with a yield after machining of over 75% of the original charge. The major losses occurred in the pouring spout-and-cup asserably. This loss is relatively unaffected by the casting length; and, therefore, castings of greater length than 26 in. should result in even greater recoveries. (auth)