Epitaxial SrRuO{sub 3} thin films were grown on SrTiO{sub 3}, (LaAlO{sub 3}){sub 0.3}(SrAlO{sub 3}){sub 0.7} and LaAlO{sub 3} substrates inducing different biaxial compressive strains. Coherently strained SrRuO{sub 3} films exhibit enhanced magnetization compared to previously reported bulk and thin film values of 1.1-1.6 {micro}{sub B} per formula unit. A comparison of (001) and (110) SrRuO{sub 3} films on each substrate indicates that films on (110) oriented have consistently higher saturated moments than corresponding (001) films. These observations indicate the importance of lattice distortions in controlling the magnetic ground state in this transitional metal oxide.

In situ mechanical testing coupled with imaging using high-energy synchrotron x-ray diffraction or tomography imaging is gaining in popularity as a technique to investigate micrometer and even sub-micrometer deformation and fracture mechanisms in mineralized tissues, such as bone and teeth. However, the role of the irradiation in affecting the nature and properties of the tissue is not always taken into account. Accordingly, we examine here the effect of x-ray synchrotron-source irradiation on the mechanistic aspects of deformation and fracture in human cortical bone. Specifically, the strength, ductility and fracture resistance (both work-of-fracture and resistance-curve fracture toughness) of human femoral bone in the transverse (breaking) orientation were evaluated following exposures to 0.05, 70, 210 and 630 kGy irradiation. Our results show that the radiation typically used in tomography imaging can have a major and deleterious impact on the strength, post-yield behavior and fracture toughness of cortical bone, with the severity of the effect progressively increasing with higher doses of radiation. Plasticity was essentially suppressed after as little as 70 kGy of radiation; the fracture toughness was decreased by a factor of five after 210 kGy of radiation. Mechanistically, the irradiation was found to alter the salient toughening mechanisms, manifest by the …