The hydration behavior of the calcium aluminates as a function of the glass content, the curing temperature, and the water-solid ratio was investigated. In order to keep them from influencing the results, the free-lime content and the surface area of all samples were kept constant, whenever possible. Samples were hydrated with a water-solid ratio of 10/1 for periods of 1 to 90 days. Three curing temperatures were studied; 2°C, 25°C, and 50°C. Samples were hydrated in tightly sealed polyethylene containers to prevent reactions with atmospheric carbon dioxide. The hydration was followed by X-ray diffraction and thermal analysis. Only two samples, Hexacalcium Tetra-alumino Magnesium Silicate and Tricalcium Magnesium Dialuminate, were successfully prepared in an amorphous form. These compounds were used to investigate the effect of glass content on the hydration behavior. Results indicate that when the glass content is increased a corresponding increase is found in the percent combined water. Samples hydrated at 25°C were influenced by changes in the glass content to a greater degree than were those hydrated at either 2°C or 50°C. The effect of the water-solid ratio on the hydration behavior of the calcium aluminates was studied using the compounds; Hexacalcium Tetra-Alumino Magnesium Silicate/ and Dodecacalcium Hepta-Aluminate. …

This investigation is concerned with determining whether a carbon substituent or a silicon substituent on the carbon terminus of a silicon-carbon double bond has a more stabilizing effect. Two different 2-substituted silaethylenes were generated at the same time by pyrolyzing 1, 1-dimethyl-2-neopentyl-4- (dimethylalkoxysilyl) silacyclobutanes in a nitrogen flow system. The results of these pyrolyses, both neat and in the presence of a trapping reagent, show that the silaethylene with a silicon substituent on the carbon terminus was favored approximately two to one over the silaethylene with a carbon substituent. This datum, along with other observations and hypotheses discussed, leads to the suggestion that the silicon substituenton the carbon terminus of the silaethylene bond has a more stabilizing effect than the carbon substituent.