The hydration behavior of the calcium aluminates as a function of the glass content, the curing temperature, and the water-solid ratio was investigated. In order to keep them from influencing the results, the free-lime content and the surface area of all samples were kept constant, whenever possible. Samples were hydrated with a water-solid ratio of 10/1 for periods of 1 to 90 days. Three curing temperatures were studied; 2°C, 25°C, and 50°C. Samples were hydrated in tightly sealed polyethylene containers to prevent reactions with atmospheric carbon dioxide. The hydration was followed by X-ray diffraction and thermal analysis. Only two samples, Hexacalcium Tetra-alumino Magnesium Silicate and Tricalcium Magnesium Dialuminate, were successfully prepared in an amorphous form. These compounds were used to investigate the effect of glass content on the hydration behavior. Results indicate that when the glass content is increased a corresponding increase is found in the percent combined water. Samples hydrated at 25°C were influenced by changes in the glass content to a greater degree than were those hydrated at either 2°C or 50°C. The effect of the water-solid ratio on the hydration behavior of the calcium aluminates was studied using the compounds; Hexacalcium Tetra-Alumino Magnesium Silicate/ and Dodecacalcium Hepta-Aluminate. …

Precipitates of a series of alkaline earth metal (barium and strontium) carbonates, chromates, phosphates, and sulfates were formed at high supersaturation by diffusion through silica hydrogel, agarose hydrogel, and the freshly developed agarosesilica mixed gels. The reaction vessels could be a small test tube, a recently designed standard micro slide cassette and a enlarged supercassette. Homogeneous nucleation is thought to have taken place, and particle development led to the formation of an unusual category of materials, known as Induced Morphology Crystal Aggregates [IMCA], at high pH under far-from-equilibrium conditions. Standard procedures were developed in order to produce homogeneous gels. Particle development led to characteristic style of pattern formation, which I have called monster, spiral, and flake. Among these IMCA, barium carbonate, chromate, and sulfate were moderately easy to grow. Barium phosphate was very difficult to grow as IMCA due to formation of poorly crystalline spherulites. IMCA of strontium carbonate, chromate and sulfate could be developed at high basic pH in the presence of silicate. Strontium carbonate sheet morphology displays a unique property, double internal layer structure, which was identified by backscattering electron imaging (BEI). Selected electron diffraction (SAD) revealed a new crystal phase which was called "Dentonite". Precipitate particles were …