A flexible nanofibrous PVDF-BaTiO3 composite material is prepared for impact sensing and biomechanical energy harvesting applications. Dielectric polyvinylidene fluoride (PVDF) and barium titanate (BaTiO3)-PVDF nanofibrous composites were made using the electrospinning process based on a design of experiments approach. The ultrasonication process was optimized using a 2k factorial DoE approach to disperse BaTiO3 particles in PVDF solution in DMF. Scanning electron microscopy was used to characterize the microstructure of the fabricated mesh. The FT-IR and Raman analysis were carried out to investigate the crystal structure of the prepared mesh. Surface morphology contribution to the adhesive property of the composite was explained through contact angle measurements. The capacitance of the prepared PVDF- BaTiO3 nanofibrous mesh was a more than 40% increase over the pure PVDF nanofibers. A comparative study of dielectric relaxation, thermodynamics properties and impact analysis of electrospun polyvinylidene fluoride (PVDF) and 3% BaTiO3-PVDF nanofibrous composite are presented. The frequency dependent dielectric properties revealed micro structural features of the composite material. The dielectric relaxation behavior is further supported by complex impedance analysis and Nyquist plots. The temperature dependence of electric modulus shows Arrhenius type behavior. The observed non-Debye dielectric relaxation in electric loss modulus follows a thermally activated process which …